为了降低固化温度,简化固化工艺,在聚三唑树脂(PTA)体系中加入三苯基磷溴化亚铜作为催化剂,根据催化剂的用量与凝胶时间的关系,确定催化剂用量为最少单体摩尔量的3‰.在催化条件下,按照50℃/6h+ l00℃/2h+ 150℃/2h的固化程序模压制备复合材料(C-PTA/T300B),研究了催化剂对复合材料玻璃化转变温度(Tg)、热稳定性(Td5)和力学性能的影响.结果表明,与未催化复合材料(PTA/T300B)相比,在力学性能保持不变的前提下,C-PTA-T300B复合材料的固化温度降低了30℃,后处理工艺得到极大简化;Tg提高了21℃;空气中Td5提高了10℃,氮气中Td5提高了5℃.
参考文献
| [1] | 陈祥宝.先进复合材料低成本技术[M].北京:化学工业出版社,2004.,2004. |
| [2] | 陈祥宝.先进树脂基复合材料扩大应用的关键[J].高科技纤维与应用,2002(06):1-5,24. |
| [3] | F.J.Doemer,R.M.Smith.Low temperature/low pressure processing of composite materials[C].41 st International SAMPE Symposium/Exhibition,1996.35-46.,1996. |
| [4] | Chris Ridgard.Affordable production of composite parts using low temperature curing prepregs[C].42 nd International SAMPE Symposium and Exhibition,1996.147-161.,1996. |
| [5] | 陈祥宝.高性能树脂基体[M].北京:化学工业出版社,1999.,1999. |
| [6] | P.S.Martin.Low temperature curing epoxy[P].US Pat.4297254,1981.,1981. |
| [7] | R.D.Hermanson.Low exotherm,low temperature curing epoxy impregnants[P].US Pat.5350779,1994.,1994. |
| [8] | Y.H.Hu,Y.H.Luo,L.Q.Wan et al.1,3-Dipolar cycloaddition polymerization of bispropargyl ether of bisphenol-A with 4,4'-biphenyl dibenzyl azide and their thermal analyses[J].Acta Polym.Sin.,2005,(4):560-565.,2005. |
| [9] | L.Q.Wan,Y.H.Luo,Y.H.Hu,et al .Synthesis and characterization of a novel polytriazole containing 1,2,3-triazole[J].Polym Prepr.,2005,46(2):1014.,2005. |
| [10] | 罗永红,扈艳红,万里强,薛莲,周围,黄发荣,沈学宁,齐会民,杜磊,陈祥宝.N,N,N′,N′-四炔丙基-4,4′-二氨基-二苯甲烷与4,4′-联苯二苄叠氮固化动力学研究[J].高等学校化学学报,2006(01):170-173. |
| [11] | 黄建智,万里强,田建军,赵占峰,王晓飞,扈艳红,黄发荣,杜磊.1,3-二（炔丙基氧）苯与4,4'-二叠氮甲基联苯的聚合反应及聚合物性能的研究[J].化学学报,2007(22):2629-2634. |
| [12] | G.Molteni,C.L.Bianchi,G.Marinoni,et al.Cu/Cu-oxide nanoparticles as catalyst in the " click" azide-alkyne cycloaddition[J].New Chem.,2006,(30),1137-1139.,2006. |
| [13] | S.Binauld,F.Boisson,T.Hamaide,et al .Kinetic study of copper (Ⅰ)-catalyzed click chemistry step-growth polymerization[J].Polym.Sci.:Part A:Polym.Chem.,2008,46 |
| [14] | L.Zhang,X.G.Chen,P.Xue,etal .Ruthenium-catalyzed cycloaddition of alkynes and organic azides[J].Am.Chem.Soc.,2005,127 |
| [15] | L .K.Rasmussen,B.C.Boren,V.V.Fokin.Ruthenium-catalyzed cycloaddition of aryl azides and alkynes[J].Org.Lett.,2007,9(26):5337-5339.,2007. |
| [16] | 李敏,张佐光,李艳霞,顾轶卓.复合材料层板热压工艺参数的分析与优化[J].材料工程,2007(z1):106-110. |
| [17] | 周浩,李瑜婧,万里强,鄂彦鹏,黄发荣,杜磊.石英纤维增强聚三唑树脂复合材料性能研究[J].玻璃钢/复合材料,2013(06):81-84. |
| [18] | 毕向军,李宗慧,唐泽辉,李薇.基于压力的树脂基复合材料成型工艺设计[J].玻璃钢/复合材料,2010(01):86-88. |
| [19] | 樊在霞,张瑜.纤维增强热塑性树脂基复合材料的加工方法[J].玻璃钢/复合材料,2002(04):22-24,5. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%