SiO2骨架支撑MoOx催化剂用于正庚烷异构化反应

催化学报 , 2003, 24(7): 549-552.

SiO2骨架支撑MoOx催化剂用于正庚烷异构化反应

柴松海 ^1, , 王新平 ^2, , 汪颖军 ^3, , 蔡天锡 ^4,

1.大连理工大学精细化工国家重点实验室,辽宁大连,116012

2.大连理工大学精细化工国家重点实验室,辽宁大连,116012

3.大连理工大学精细化工国家重点实验室,辽宁大连,116012

4.大连理工大学精细化工国家重点实验室,辽宁大连,116012

基金项目: 中国石油化工集团总公司资助项目(X500002)

关键词：正庚烷 , 异构化 , 氧化钼 , 二氧化硅 , 骨架 , 中孔

n-Heptane Isomerization on MoOx Catalyst Supported by SiO2 as a Framework

采用SEM,XRD,EDS及N2吸附-脱附方法研究了骨架型MoOx-SiO2催化剂和负载型MoOx/SiO2催化剂的物理化学结构,并在常压固定床流动反应器上考察了两种催化剂对正庚烷异构化反应的催化性能. 结果表明,在MoOx-SiO2催化剂中,44.6%的SiO2即可起到很好的骨架支撑作用; MoOx晶相以足够大的空间区域聚集包裹在SiO2骨架中,形成类似MoOx催化剂的独特的中孔结构. 与MoOx催化剂相比,MoOx-SiO2催化剂显著提高了机械强度,并维持了MoOx催化剂较高的活性和选择性. 由于钼物种和载体之间的相互作用,负载型MoOx/SiO2催化剂表现出较低的比活性. 脉冲注入H2S实验结果表明,MoOx-SiO2催化剂具有较好的抗硫性能.

参考文献

[1]	Wang Z B;Kamo A;Yoneda T;Komatsu T Yashima T .[J].Applied Catalysis A:General,1997,159:119.
[2]	Arribas MA.;Martinez A.;Marquez F. .Activity, selectivity, and sulfur resistance of Pt/WOx-ZrO2 and Pt/Beta catalysts for the simultaneous hydroisomerization of n-heptane and hydrogenation of benzene[J].Journal of Catalysis,2000(2):309-319.
[3]	Falco M.G. .Influence of Pt concentration on tungsten oxide-promoted zirconia during n-hexane isomerization[J].Applied Catalysis, A. General: An International Journal Devoted to Catalytic Science and Its Applications,2000(1):37-43.
[4]	缪长喜;华伟明;高滋 .[J].催化学报,1997,18(01):13.
[5]	Iglesia E;Ribeiro F H;Boudart M;Baumgartner J E .[J].Catalysis Today,1992,15(02):307.
[6]	Blekkan E A;Pham-Huu C;Ledoux M J .[J].Industrial and Engineering Chemistry Research,1994,33(07):1657.
[7]	York A P E;Pham-Huu C;Del Gallo P;Ledoux M J .[J].Catalysis Today,1997(35):51.
[8]	Matsuda T;Shiro H;Sakagami H;Takahashi N .[J].Catalysis Letters,1997,47(02):99.
[9]	Katrib A;Mey D;Maire G .[J].Catalysis Today,2001(65):179.
[10]	WANG Y J;Wang X P;Chai S H;Cai T X .[J].Reaction Kinetics and Catalysis Letters,2002,77(01):125.
[11]	Ying Jun WANG,Xin Ping WANG,Tian Xi CAI.Effect of Ni Loading on the Catalytic Properties of Molybdenum Oxides for the Isomerization of Heptane[J].中国化学快报(英文版),2002(02):177-180.
[12]	Matsuda T;Hanai A;Uchijima F;Sakagami H,Takahashi N .[J].Microporous and Mesoporous Materials,2002,51(02):155.
[13]	Delporte P;Meunier F;Pham-Huu C;Vennegues P,Ledoux M J,Guille J .[J].Catalysis Today,1995,23(03):251.
[14]	Barath F;Turki M;Keller V;Maire G .[J].Journal of Catalysis,1999,185(01):1.

上一张下一张

计量

下载量()
访问量()

作者相关

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网