Thermodynamic assessment of Ti-Co-Cu ternary system has been carried out by combining first-principle calculation and CALPHAD method. Firstly, formation enthalpies of stable and hypothesized compounds were calculated by first-principles method. Then, based on reported experimental information, a thermodynamic description of the Ti-Co-Cu ternary system was performed. Solution phases were treated as substitutional solutions of which excess Gibbs energies were formulated by Redlich-Kister polynomial, and the intermediate phases were described with sublattice models. All measured isothermal sections were reasonably reproduced. In addition, liquidus projection of this ternary system was further calculated, which may be useful for relevant materials processing.

参考文献

[1]
[2]
[3]
[4]
[5]
[6] I.S. Batra, A. Laik, G.B. Kale, G.K. Dey and U.D. Kulkarni: Mater. Sci. Eng. A, 2005, 402, 118.
[2] Y.M. Wang, H.S. Liu, Q. Chen, F. Zheng and Z.P. Jin: J. Alloy. Compd, 2007, 439, 196.
[3] H.S. Liu, Y.M. Wang, L.G. Zhang, Q. Chen, F. Zheng and Z.P. Jin: J. Mater. Res, 2006, 21, 2493.
[4] Y.M. Wang, H.S. Liu, L.G. Zhang, Q. Chen, F. Zheng and Z.P. Jin: Mater. Sci. Eng. A, 2006, 431, 184.
[5]H.H. Xu, Y. Du, B.Y. Huang, Z.P. Jin, S Li and X. Zhang: Z. Metallkd., 2006, 97, 140.
[6] M. Palumbo, S. Curiotto and L. Battezzati: CALPHAD, 2006, 30, 171.
[7] G. Cacciamani, R. Ferro, I. Ansara and N. Dupin: Intermetallics, 2000, 8, 213.
[8] A.V. Davydov, U.R. Kattner, D. Josell, R.M. Waterstrat, W.J. Boettinger, J.E. Blendell, A.J. Shapiro and W.J. Boettinger: Metall. Mater. Trans. A, 2001, 32, 2175.
[9]C. Hari Kumar, I. Ansara, P. Wollants and L. Delaey: Z. Metallkd., 1996, 87, 666.
[10]P. Canale and C. Servant: Z. Metallkd., 2002, 93, 273.
[11] Hu. Pfeifer, S. Bhan and K. Schubert: J. Less Common Met, 1968, 14, 291.
[12]K.P. Gupta: Indian Institute of Metals, Calcutta, India, 1990, 228.
[13] G. Ghosh and M. Asta: Acta Mater, 2005, 53, 3225.
[14] G. Ghosh: Acta Mater, 2007, 55, 3347.
[15] G. Kresse and J. Furthmuller: Phys. Rev. B, 1996, 54, 11169.
[16] G. Kresse and J. Furthmuller: Comput. Mater. Sci, 1996, 6, 15.
[17] J.P. Perdew and Y. Wang: Phys. Rev. B, 1992, 45, 13244.
[18] J.P. Perdew, J.A. Chevary, S.H. Vosko, K.A. Jackson, M.R. Pederson, D.J. Singh and C. Fiolhais: Phys. Rev. B, 1992, 46, 6671.
[19] A.T. Dinsdale: CALPHAD, 1991, 15, 317.
[20]Y.M. Muggianu, M. Gambino and J.P. Bros: J. Chim. Phys., 1975, 22, 83.
[21] O. Redlich and A.T Kister: Ind. Eng. Chem, 1948, 40, 345.
[22]M. Hillert and L.I. Sta®
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%