针对通钢FTSR薄板坯连铸连轧生产线生产集装箱板SPA—H产生边部缺陷的问题，通过研究分析缺陷产生的机制，优化二冷水给水模式提高连铸坯边角温度、更换辊子不转的扇形段、清理氧化铁皮降低夹持辊扭矩、实施多段缓慢压下及降低钢水中酸溶铝和氮含量等控制措施，使集装箱板SPA—H热轧板卷的边部缺陷得到有效控制。
The causes of edge defects on container strips produced by FTSR thin slab casting machine in Tonghua Iron and Steel Co. , Ltd. were analyzed. The edge defects ratio of container strips was effectively controlled by optimization of second cooling water, changing the segments with fail rollers on time, removing scale between segment rollers to decrease torsion of pinch rolls, reducing the soft reduction roller gaps by multiple steps, and controlling ω（[N]） and ω（[N]） in the molten steel.
参考文献
| [1] | Kwon O D;Choi J;Lee I R et al.Optimization of Mold Os-cillation Pattern for the Improvement of Surface Quality and Imbrication in Slab Continuous Casting[J].Steelmaking Conference Processings,1991,74:561. |
| [2] | Kawakami K;Kitagawa T;Komatsu M et al.Study on the Solidification Phenomena in Continuous Casting Mold[R].Tokyo:Nippon Kokan Technical,1982. |
| [3] | McPherson N A;Mercer R E.Continuous Casting of Slabs at BSC Ravenscraig Works[J].Ironmaking and Steelmaking,1980(04):167. |
| [4] | Harada S;Tanaka S;Misumi H et al.A Formation Mecha-nism of Transverse Cracks on CC Slab Surface[J].ISIJ International,1990,30(04):310. |
| [5] | Yasunaka H;Nakayama K;Ebina K et al.Improvement of Transverse Corner Cracks in Continuously Cast Hypoperitee-tic Siabs[J].Tetsu To Hagane-Journal of the Iron and Steel Institute of Japan,1995,81(09):894. |
| [6] | Koichi Yamamoto;Hirowo G;Suzuki et al.Formation Mechanism and Prevention Method of Facial Cracks of Con-tinuously Cast Steel Slabs Containing Boron[J].Tetsu To Hagane-Journal of the Iron and Steel Institute of Japan,1987,73(01):115. |
| [7] | Mintz B .Hot Ductility of Directly Cast C-Mn-Nb-A1 Steel[J].Materials Science and Technology,1986,2(06):589. |
| [8] | Yoshie A;Fujioka M;Watanabe A et al.Modeling of Mi-crostructural Evolution and Mechanical Properties of Steel Plates Produced by Thermo-Mechanieal Control Process[J].ISIJ International,1992,32(03):395. |
| [9] | Medina S F;Mancilla J E .Static Recrystailization Modeling of Hot Deformed Steels Containing Several Alloying EIements[J].ISIJ International,1996,36(08):1070. |
| [10] | 洪兵雄,张国广.用CSP连铸机生产集装箱板钢工艺研究[J].钢铁,2004(z1):455-458. |
| [11] | Mintz Barrie .The Influence of Composition on the Hot Ductility of Steels and to the Problem of Transverse Cracking[J].ISIJ International,1999,39(09):833. |
| [12] | 傅杰;周德光;李晶 等.低碳超级钢中氧硫氮的控制及其对钢组织性能的影响[J].云南大学学报（自然科学版）,2002,24(z1):158. |
| [13] | Burden M H;Funnell G D;Whitaker A G.Solidifica-tion and Casting of Metals[M].London:The Metals Society,1979 |
| [14] | Wolf M M .Effects of Tramp Element in Continuous Casting[J].Ironmaking and Steelmaking,1985,12(06):299. |
| [15] | Crowther 13 N;Green M J W;Mitchell P S.The Influence oi Composition on the Hot Cracking Susceptibility During Cast-ing of Microalloyed Steels Processed to Simulate Thin Slab Casting Conditions[J].Materials Science Forum,1998:284. |
| [16] | Wigman S L;Millet M D.Demands on Refining Processes in Thin Slab Casting[A].Lulea,1992 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%