通过采用电化学性能测试、极化测试和电化学阻抗测试等方法评价了研制的深海牺牲阳极在模拟深海环境中的性能,并与常规环境进行对比.结果表明,深海阳极在模拟深海环境中的电流效率达95％,实际电容量大于2 700 A·h/kg,工作电位接近-1.1V,溶解形貌良好,腐蚀产物脱落,整体电化学性能优异,但受深海低温低氧环境影响,深海阳极在模拟深海环境中的发出电流量及反应活性略低于常规环境.
参考文献
| [1] | Venkateshan R, Venkatasamy M A, Bhaskmn T A.Corrosion of ferrous alloys in deepsea environment[J].British Corrosion Journal, 2002, 37 (4):257-266.,2002. |
| [2] | Chen S, Hartt W,Wolfson S.Deep water cathodic protection:Part2-Field deploymem results[J].Corrosion,2003 (8):721-732.,2003. |
| [3] | Schrieber C F, Murray R W .Effect of hostile marine environments on the Al-Zn-In-Si sacrificial anode[J].Materials Protection,1988,27(7):70-77.,1988. |
| [4] | 贾红刚.模拟深海环境对铝基牺牲阳极电化学性能的影响研究[J].现代制造技术与装备,2014(04):24-25. |
| [5] | 孙海静,刘莉,李瑛.深海静水压力环境下低合金高强度钢腐蚀行为研究[J].电化学,2013(05):418-424. |
| [6] | Tawns A, Oakley R.Cathodic protection at a simulated depth of 2500m[R].NACE,2000, No.00134.,2000. |
| [7] | DNV-RP-F103-2010,Cathodic protection of submarine pipelinses by galvanic anodes[S].DET NORSKE VERITAS,2010.,2010. |
| [8] | 余波,孙明先,闫永贵,马力.镁含量对Al-Zn-In-Mg-Ti-Ga-Mn合金牺牲阳极组织和性能的影响[J].材料开发与应用,2012(03):56-59. |
| [9] | 李威力,闫永贵,陈光,马力.合金元素对铝基牺牲阳极性能的影响[J].中国腐蚀与防护学报,2012(02):127-132. |
| [10] | 李威力,闫永贵,陈光,马力.Al-Zn-In系牺牲阳极低温电化学性能研究[J].腐蚀科学与防护技术,2009(02):122-124. |
| [11] | 翁松干.合金成分及海洋环境对Al-Zn-In-Mg-Ti牺牲阳极电化学性能影响研究[D].青岛:中国海洋大学,2012.,2012. |
| [12] | 胡胜楠 .模拟深海环境下Al-Zn-In牺牲阳极性能研究[D].哈尔滨工程大学,2012. |
| [13] | 李威力 .新型深海铝合金牺牲阳极研制及性能研究[D].南京理工大学,2012. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%