采用化学沉淀法-水热法制备β-TCP/HA双相陶瓷粉末,通过调节水热温度和水热时间,将制备的粉体于900℃下煅烧,得到了不同配比的β-TCP/HA双相陶瓷粉末.研究表明,煅烧前的粉末主要为缺钙的HA相,随着水热温度的升高和水热时间的延长,煅烧后得到的粉末中HA的相含量不断增多.煅烧前为短棒状的缺钙型和稳定型的HA,煅烧后,β-TCP的晶粒呈球形,短棒状的HA随水热温度的升高和时间的延长而逐渐增多,且温度升高的影响比延长时间的影响更为显著.
参考文献
| [1] | Daniel L Alge;W Scott Goebel;Tien-Min Gabriel Chu .In vitro degradation and cytocompatibility of dicalcium phosphate dihydrate cements prepared using the monocalcium phosphate monohydrate/hydroxyapatite system reveals rapid conversion to HA as a key mechanism.[J].Journal of biomedical materials research, Part B. Applied biomaterials,2012(3):595-602. |
| [2] | Horch HH;Sader R;Pautke C;Neff A;Deppe H;Kolk A .Synthetic, pure-phase beta-tricalcium phosphate ceramic granules (Cerasorb) for bone regeneration in the reconstructive surgery of the jaws.[J].International journal of oral and maxillofacial surgery,2006(8):708-713. |
| [3] | Neamat A;Gawish A;Gamal Eldeen AM .beta-Tricalcium phosphate promotes cell proliferation, osteogenesis and bone regeneration in intrabony defects in dogs.[J].Archives of Oral Biology,2009(12):1083-1090. |
| [4] | Xie Y;Chopin D;Morin C;Hardouin P;Zhu Z;Tang J;Lu J .Evaluation of the osteogenesis and biodegradation of porous biphasic ceramic in the human spine.[J].Biomaterials,2006(13):2761-2767. |
| [5] | 刘同军 .β-TCP/HAP复合生物陶瓷的制备[D].天津大学,2006. |
| [6] | R. Z. LEGEROS;S. LIN;R. ROHANIZADEH;D. MIJARES;J. P. LEGEROS .Biphasic calcium phosphate bioceramics: preparation, properties and applications[J].Journal of Materials Science. Materials in Medicine,2003(3):201-209. |
| [7] | 丑修建 .组织工程复相（羟基磷灰石+β-磷酸三钙）多孔陶瓷支架材料的制备研究[D].昆明理工大学,2005. |
| [8] | 王辛龙 .纳米磷酸钙生物陶瓷的制备及其生物学效应研究[D].四川大学,2006. |
| [9] | Loo SCJ;Siew YE;Ho S;Boey FYC;Ma J .Synthesis and hydrothermal treatment of nanostructured hydroxyapatite of controllable sizes[J].Journal of Materials Science. Materials in Medicine,2008(3):1389-1397. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%