使用硫酸镍作为化学镀镍磷镀液的主盐,直接在AZ91D镁合金基体上化学镀镍.使用扫描电镜和X射线衍射技术分析镀层的表面形貌和组织.化学镀镍磷镀层是致密的,无明显缺陷,其磷含量约为3.72 mass%.化学镀镍磷镀层的显微硬度值约为660 VHN,化学镀镍的沉积速度为23 μm/h.前处理过程中的酸洗步骤使镁合金基体产生粗糙的表面,从而使镀层和基体之间起到了互锁的作用,增加了镀层的结合力.
参考文献
| [1] | Froes F H;Ward - Close C M.Processing of light metals for enhanced performance[J].Journal of Materials Processing Technology,1995(48):667. |
| [2] | Guang Ling Song;Andrej Atrens .Corrosion mechanisms of magnesium alloys[J].Advanced Engineering Materials,1999(1):11-33. |
| [3] | Gray J E;Luan B.Protective coatings on magnesium and its alloys - a critical review[J].Journal of Alloys and Compounds,2002(336):88. |
| [4] | Miller R E.Trends in the electroless nickel industry[J].Plating and Surface Finishing,1987(74):52. |
| [5] | Keen R H.Application and control of electroless nickel processes at Northwest Airlines[J].Plating and Surface Finishing,1988(75):22. |
| [6] | Ambat R.;Zhou W. .Electroless nickel-plating on AZ91D magnesium alloy: effect of substrate microstructure and plating parameters[J].Surface & Coatings Technology,2004(2/3):124-134. |
| [7] | Shahin G E.Electroless nickel on magnesium alloy automotive parts[J].Automotive Finishing,2001:12. |
| [8] | Sharma A K;Suresh M R;Bhojraj H.Electroless nickel plating on magnesium alloy[J].Metal Finishing,1998(96):10. |
| [9] | 霍宏伟,李瑛,王福会.AZ91D镁合金化学镀镍[J].中国腐蚀与防护学报,2002(01):14-17. |
| [10] | 向阳辉,胡文彬,沈彬,赵昌正,丁文江.镁合金直接化学镀镍的初始沉积机制[J].上海交通大学学报,2000(12):1638-1640. |
| [11] | ASTM Standards B733- 97. Standard Specification for Autocatalytic (Electroless) Nickel- Phosphorus Coatings on Metal[S]. |
| [12] | Chen BH;Hong L;Ma Y;Ko T M.Effects of surfactants in an electroless nickel - plating bath on the properties of Ni - P alloy deposits[J].Industrial and Engineering Chemistry Research,2002(41):2668. |
| [13] | 刘新宽,向阳辉,胡文彬,丁文江.镁合金化学镀镍层的结合机理[J].中国腐蚀与防护学报,2002(04):233-236. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%