Evaluation of Microstructure and Mechanical Property of FSW Welded MB3 Magnesium Alloy

钢铁研究学报(英文版), 2006, 13(4): 75-78.

^1, , ^2, , ^3, , ^4, , ^5,

1.Metallurgical Engineering Department, Xi′an University of Architecture and Technology, Xi′an 710055, Shaanxi, China

2.Metallurgical Engineering Department, Xi′an University of Architecture and Technology, Xi′an 710055, Shaanxi, China

3.Metallurgical Engineering Department, Xi′an University of Architecture and Technology, Xi′an 710055, Shaanxi, China

4.Metallurgical Engineering Department, Xi′an University of Architecture and Technology, Xi′an 710055, Shaanxi, China

5.State Key Laboratory for Mechanical Behavior of Material, Xi′an Jiao Tong University, Xi′an 710049, Shaanxi, China

Evaluation of Microstructure and Mechanical Property of FSW Welded MB3 Magnesium Alloy

Keywords： friction stir welding

An experiment was carried out on the friction stir welding of MB3 magnesium alloy to determine welding parameters for obtaining an excellent weld appearance without void, cracking, or distortion. Frictional heat and plastic flow created fine and equiaxed grains in the weld nugget, and the elongated and recovered grains in the thermomechanically affected zone (TMAZ). The grains in the heat affected zone (HAZ) grow slightly. The mechanical property results show that maximum joint tensile strength can reach 97.2% of the parent material, which is stronger than that of fusion joints; and the failure almost occurs in the heat affected zone.

参考文献

[1]	Brook C R;DING Fu trans.Non-Ferrous Metal Heat Treatment Microstructureand Property[M].北京:冶金工业出版社,1988
[2]	American Welding Society.Welding Manual Metal and Weld Ability[M].Miami:AWS,1995
[3]	C J Dawes .Causing a stir in welding circles[J].Sheet Metal Industries,1995(9):22,24-26-0.
[4]	Jata K.V.;Semiatin S.L. .Continuous dynamic recrystallization during friction stir welding of high strength aluminum alloys[J].Scripta materialia,2000(8):743-749.
[5]	S.Benavides;Y.Li;L.E.Murr;D.Brown;J.C.McClure .Low-temperature friction-stir welding of 2024 aluminum[J].Scripta materialia,1999(8):809-815.
[6]	Yutaka S. Sato;Mitsunori Urata;Hiroyuki Kokawa .Retention of fine grained microstructure of equal channel angular pressed aluminum alloy 1050 by friction stir welding[J].Scripta materialia,2001(1):109-114.
[7]	Sutton M A;Yang B;Reynolds A P et al.Microstructural Studies of Friction Stir Welds in 20242T3 Aluminum[J].Materials Science and Engineering,2002,323(03):160-166.
[8]	Hanadi G. Salem;Anthony P. Reynolds;Jed S. Lyons .Microstructure and retention of superplasticity of friction stir welded superplastic 2095 sheet[J].Scripta materialia,2002(5):337-342.
[9]	Li Y.;Murr LE.;Trillo EA. .Friction-stir welding of aluminum alloy 2024 to silver[J].Journal of Materials Science Letters,2000(12):1047-1051.
[10]	Park SHC.;Sato YS.;Kokawa H. .Microstructural evolution and its effect on Hall-Petch relationship in friction stir welding of thixomolded Mg alloy AZ91D[J].Journal of Materials Science,2003(21):4379-4383.
[11]	J. A. Esparza;W. C. Davis;E. A. Trillo;L. E. Murr .Friction-stir welding of magnesium alloy AZ31B[J].Journal of Materials Science Letters,2002(12):917-920.
[12]	Seung Hwan C. Park;Yutaka S. Sato;Hiroyuki Kokawa .Effect of micro-texture on fracture location in friction stir weld of Mg alloy AZ61 during tensile test[J].Scripta materialia,2003(2):161-166.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Evaluation of Microstructure and Mechanical Property of FSW Welded MB3 Magnesium Alloy

参考文献