采用不超过1 kW/kg的搅拌功率制备出7A04铝合金大体积半固态浆料，研究浇注温度、搅拌功率和搅拌时间对7A04铝合金大体积半固态浆料组织的影响。结果表明：在本实验条件下，随着浇注温度的降低、搅拌功率的增加和搅拌时间的延长，7A04铝合金大体积半固态浆料初生α(Al)的晶粒尺寸变得细小，晶粒平均圆整度先增加后保持平稳；在浇注温度650℃、名义搅拌功率0.6 kW/kg和搅拌时间40 s条件下可以制备出初生晶粒平均直径为73.5μm、平均圆整度为0.57的7A04大体积铝合金半固态浆料。
The large-volume semi-solid slurry of 7A04 aluminum alloy was prepared by electromagnetic stirring with power of less than 1 kW/kg, and the effects of pouring temperature, stirring power and stirring time on the slurry were investigated. The results indicate that primaryα(Al) particles of large-volume semi-solid slurry of 7A04 aluminum alloy becomes finer, and average shape factor first increases and then keeps stable with decreasing pouring temperature, increasing stirring power and stirring time under the condition of this work. The large-volume semi-solid slurry of 7A04 aluminum alloy with primaryα(Al) particles of average equivalent diameter of 73.5μm and average shape factor of 0.57 is obtained under pouring temperature of 650℃, nominal stirring power of 0.6 kW/kg and stirring time of 40 s.
参考文献
| [1] | James C. Williams;Edgar A. Starke Jr..Progress in structural materials for aerospace systems[J].Acta materialia,200319(19):5775-5799. |
| [2] | GUO Hong-min;YANG Xiang-jie;WANG Jia-xuan;HU Bin;ZHU Guang-lei.Effects of rheoforming on microstructures and mechanical properties of 7075 wrought aluminum alloy[J].中国有色金属学报（英文版）,2010(03):355-360. |
| [3] | 张军;康永林;张帆.A356铝合金半固态流变压铸件力学性能的研究[J].特种铸造及有色合金,2011(8):718-720. |
| [4] | 李亚庚;毛卫民;朱文志;杨斌;宋晓俊.机械搅拌对半固态7075铝合金浆料组织的影响[J].特种铸造及有色合金,2015(7):717-719. |
| [5] | Yang Bin;Mao Weimin;Song Xiaojun.Microstructure characteristics and mechanical properties of rheocasting 7075 aluminum alloy[J].中国铸造,2013(05):277-281. |
| [6] | L Zhang;W.Li;J.P. Yao.Microstructures and thermal stability of the semi-solid 2024 aluminum alloy prepared using the pulsed magnetic field process: Effects of technological parameters[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2013:156-161. |
| [7] | 刘政;毛卫民;赵振铎.用新工艺制备半固态铝合金浆料[J].材料研究学报,2006(2):125-130. |
| [8] | 朱艳丽;赵君文;李微;朱振宇;戴光泽;张鲲.电磁搅拌对7A04铝合金大体积半固态浆料组织的影响[J].中国有色金属学报,2014(11):2735-2742. |
| [9] | 董杰;路贵民;任栖锋;崔建忠.液相线铸造法非枝晶半固态组织形成机理探讨[J].金属学报,2002(2):203-207. |
| [10] | 李涛;黄卫东;林鑫.半固态处理中球晶形成与演化的直接观察[J].中国有色金属学报,2000(5):635. |
| [11] | 毛卫民;甄子胜;陈洪涛.电磁搅拌对半固态AZ91D镁合金组织的影响[J].材料研究学报,2005(3):303-309. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%