The melting temperature and critical transition temperature Tc of YBa2Cu3O7-δ with deferent content additives of PbO and BaPbO3 were studied. When PbO was doped in YBa2Cu3O7-δ the melting temperature of YBa2Cu3O7-δ was reduced, however its superconductivity was weakened. From the XRD pattern of the sintered mixture of YBa2Cu3O7-δ and PbO, it was known that there was a reaction between YBa2Cu3O7-δ and PbO, and the product was BaPbO3. Hence different contents of BaPbO3 ( 10mass%, 20mass% and 30mass% ) were added in YBa2Cu3O7-δ. It was proved that there were no reactions between YBa2Cu3O7-δ and BaPbO3. And the superconductivity of the mixtures was much better than that of the samples with PbO additive.
参考文献
| [1] | G S Yuan .Physica C: Superconductivity[J].Its Applications,2000,237:91. |
| [2] | K Thangaraj;A N Iyer;L Zhang;K Salama .Superconductor Science[J].Technology,2000,13:1035. |
| [3] | S Pinol;M Najib;T Puig;X Obradors H Xuriguera M Segarra .Physica C: Superconductivity[J].Its Applications,2002,372-376:738. |
| [4] | C. L. H. Thieme;S. Fleshler;D. M. Buczek;M. Jowett;L. G. Fritzemeier;P. N. Arendt;S. R. Foltyn;J. Y. Coulter;J. O. Willis .Axial strain dependence at 77K of the critical current of thick YBaCuO films on Ni-alloy substrates with IBAD buffer layers[J].IEEE Transactions on Applied Superconductivity: A Publication of the IEEE Superconductivity Committee,1999(2 Pt.2):1494-1497. |
| [5] | R N Bhattacharya;R Noufi;L L Roybal;R K Ahrenkiel.[J].Journal of the Electrochemical Society:1643. |
| [6] | S Kohayashi;S Yoshizawa;H Miyairi;H Nakane S Nagaya.[J].Materials Science and Engineering B:Solid-state Materials for Advanced Technology:70. |
| [7] | B Roper;F Carmona;S Fl rois.[J].Applied Superconductivity:1015. |
| [8] | D E Moxey;R Kalyanaraman;A Sharma;J Narayan C B Lee J Muth.[J].Materials Research Society Symposium Proceedings:269. |
| [9] | J C Bowker;G A Whitlow.[J].Superconductor Science and Technology,1993:106. |
| [10] | J Shu;A Adnot;B P A Gr;jS Kaliaguine.[J].THIN SOLID FILMS,1996:72. |
| [11] | T Uno;K Tatsumi.[J].Journal of the Japan Institute of Metals:1545. |
| [12] | B Stadlober;P Knoll;H Jodlbauer;W Lang,N Brnicevic,R Abt,E Schweiger,G Leising ,H Kahlert.Proceedings of the International Winter School Conference[C].Tyrol,Austria,Springer-Verlag Berlin,1990:46. |
| [13] | H T Ren;L Xiao;X P Wang;R K Wang,B L Zhao,L H Sun.[J].Rare Metals,1990(01):24. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%