The localized shear deformation in the 2024 and 2124 Al matrix composites reinforced with SiC particles was investigated with a split Hopkinson pressure bar (SHPB) at a strain rate of about 2.0×103 s-1. The results showed that the occurrence of localized shear deformation is sensitive to the size of SiC particles. It was found that the critical strain, at which the shear localization occurs, strongly depends on the size and volume fraction of SiC particles. The smaller the particle size, the lower the critical strain required for the shear localization. TEM examinations revealed that Al/SiCp interfaces are the main sources of dislocations. The dislocation density near the interface was found to be high and it decreases with the distance from the particles. The Al matrix in shear bands was highly deformed and severely elongated at iow angle boundaries. The Al/SiCp interfaces, particularly the sharp corners of SiC particles,provide the sites for microcrack initiation. Eventual fracture is caused by the growth and coalescence of microcracks along the shear bands. It is proposed that the distortion free equiaxed grains with low dislocation density observed in the center of shear band result from recrystallization during dynamic deformation.
参考文献
| [1] | H Y Kim;S H Hong .[J].Scripta Materialia,1994,30:297. |
| [2] | Y H Kim;S Lee;N J Kim .[J].Metallurgical and Materials Transactions,1993,23A:2589. |
| [3] | I A Ibrahim;F A Mohamed;E J Lavernia .[J].Journal of Materials Science,1991,26:1137. |
| [4] | J.M.Papazian;P.N.Adler .[J].Metallurgical and Materials Transactions,1990,21A:401. |
| [5] | J J lewandowski;C T Liu .[J].Material Science and Engineering,1989,107:241. |
| [6] | A Marchand;J Duffy .[J].Engineering Fracture Mechanics,1988,30:295. |
| [7] | S Lee;K M Cho .[J].Metallurgical and Materials Transactions,1993,24:895. |
| [8] | R·F Recht .[J].Journal of Applied Mechanics,Transactions ASME,1964,31:189. |
| [9] | R.J.Clifton .Material Response to Ultra-high Loading Rates,National Advisory Board Committee, report NMAB 356[R].,1979. |
| [10] | Y L Bai.A Criterion for Thermoplastic Shear Instability[A].Plenum Press, New York,1981:277. |
| [11] | R J Clifton .[J].Scripta Materialia,1984,18:443. |
| [12] | M A Meyers;V F Nesterenko;Y b Xu.[J].Journal de Physique,2000(10):9. |
| [13] | Y B Xu;Y L Bai;M A Meyers .[J].Materials Science and Engineering,2001,A299:287. |
| [14] | S Lee;K-M Cho .[J].Metallurgical and Materials Transactions,1993,24A:17. |
| [15] | U Andrade;M A Meyers .[J].Acta Materialia,1995,429:2493. |
| [16] | M A Meyers .[J].Mechanics of Materials,1994,17:175. |
| [17] | Y. B. XU;Y. L. BAI;Q. XUE .FORMATION, MICROSTRUCTURE AND DEVELOPMENT OF THE LOCALIZED SHEAR DEFORMATION IN LOW-CARBON STEELS[J].Acta materialia,1996(5):1917-1926. |
| [18] | Q Li;Y B Xu;Z H Lai .[J].Materials Science and Engineering,2000,A276:250. |
| [19] | M A Meyers;Y B Xu;Q Xue.[J].Acta Materialia,2002 |
| [20] | B.Derby .[J].Acta Materialia,1991,399:955. |
| [21] | M A Meyers;J C LaSalvia.[A].Rex,96,Monterey,USA,1997:279. |
| [22] | Z Ling;L Luo .[J].Journal of Physics C:Solid State Physics,1994,C3:453. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%