采用液相共沉淀法制备球形掺镁高镍三元材料前驱体，结合高温固相法制备了氧化硼包覆高镍三元材料LiMg0.03(Ni0.77Co0.1 Mn0.1)O2?B2O3，对样品物理性能、电化学性能及安全稳定性进行分析测定，并对性能改善的机理进行分析。结果表明：通过Mg元素体相掺杂和B2O3表面包覆制备的球形高镍三元材料LiMg0.03(Ni0.77Co0.1 Mn 0.1)O 2?B 2 O 3具有良好的电化学性能和物理性能，对锂负极初始放电容量达到181 mA?h/g，对碳负极300次循环后，放电容量保持率达到92%，压实密度达到3.9 g/cm3。同时，LiMg0.03(Ni0.77Co0.1 Mn0.1)O2?B2O3具有良好的热稳定性和抗过充电的能力，在充电态下热分解温度比未掺杂和未包覆的样品提升12℃。
The spherical precursor doped with magnesium for high nickel ternary composites was prepared by a co-precipitation method in an aqueous solution. Then, LiMg0.03(Ni0.77Co0.1 Mn0.1)O2?B2O3 was prepared by solid state reaction method at high temperature. The physical property, electrochemical property and security stability of these samples were analyzed. The improvement mechanism was also discussed. The results show that the sample doped with magnesium and coated with boron oxide has excellent electrochemical and physical properties. The initial discharge capacity vs lithium anode is 181 mA?h/g, the capacity retention rate vs graphite anode is 92%after 300 cycles, and the compact density is 3.9 g/cm3. In addition, LiMg0.03(Ni0.77Co0.1 Mn0.1)O2?B2O3 has a good thermal stability and an overcharge resistant ability, its thermal decomposition temperature in state of charge rises 12 ℃ compared with the un-doped and uncoated sample.
参考文献
| [1] | 潘成迟,Craig E.BANKS,宋维鑫,王驰伟,陈启元,纪效波.正极材料LiNixCoyMnzO2的微/纳结构对锂离子电池性能改进的最新进展[J].中国有色金属学报（英文版）,2013(01):108-119. |
| [2] | 孙玉城.镍钴锰酸锂三元正极材料的研究与应用[J].无机盐工业,2014(01):1-3. |
| [3] | 蔡少伟.锂离子电池正极三元材料的研究进展及应用[J].电源技术,2013(06):1065-1068. |
| [4] | LIAO P Y;DUH J G;SHEEN S R .Microstructure and electrochemical performance of LiNi0.6Co0.4-xMnxO2 cathode materials[J].Journal of Power Sources,2005,143:212-218. |
| [5] | 王接喜,李新海,王志兴,李灵均,郭华军,岳鹏,伍凌.快速共沉淀过程pH值对Ni0.8Co0.1Mn0.1（OH）2及LiNi0.8Co0.1Mn0.1O2性能的影响[J].中国有色金属学报,2011(09):2175-2181. |
| [6] | 陈巍,李新海,王志兴,郭华军,岳鹏,李灵均.共沉淀法制备LiNi0.8Co0.1Mn0.1O2过程中加料速度对其性能的影响[J].中国有色金属学报,2012(07):1956-1962. |
| [7] | 李月涛,李刚,王茹英,刘庆国.钴包埋镍酸锂的Mg掺杂改性研究[J].电池工业,2010(06):348-350. |
| [8] | 俞会根,王恒,盛军.三元正极材料Li[Ni-Co-Mn]O2的研究进展[J].电源技术,2014(09):1749-1752. |
| [9] | ZHANG Pei-xin;ZHANG Li;REN Xiang-zhong;YUAN Qiu-hua LIU Jian-hong ZHANG Qian-ling .Preparation and electrochemical properties of LiNi1/3Co1/3Mn1/3O2-PPy composites cathode materials for lithium-ion battery[J].Synthetic Metals,2011,161:1092-1097. |
| [10] | RILEY L A;ATTA S V;CAVANAGH A S;YAN Y GEORGE S M LIU P DILLON A C LEE S H .Electrochemical effects of ALD surface modification on combustion synthesized LiNi1/3Mn1/3Co1/3O2 as a layered-cathode material[J].Journal of Power Sources,2011,196:3317-3324. |
| [11] | 邹邦坤;丁楚雄;陈春华 .锂离子电池三元正极材料的研究进展[J].中国科学:化学,2014,44(07):1104-1115. |
| [12] | OHZUKU T;UEDA A;NAGAYAMA M .Electrochemistry and structural chemistry of LiNiO2(R3m)for 4 volt secondary lithium cells[J].Journal of the Electrochemical Society,1993,140(07):1862-1870. |
| [13] | 马全新,孟军霞,杨磊,曹文.锂离子电池正极材料LiNi0.5Co0.2Mn0.3O2的制备及电化学性能[J].中国有色金属学报,2013(02):456-462. |
| [14] | 邓龙征,吴锋,高旭光,刘震天,谢海明.LiNi0.87Co0.10Mg0.03O2正极材料的合成和电化学性能[J].中国有色金属学报（英文版）,2015(02):527-532. |
| [15] | Pei-Yun Liao;Jenq-Gong Duh;Jyh-Fu Lee .Valence change and local structure during cycling of layer-structured cathode materials[J].Journal of Power Sources,2009(1):9-15. |
| [16] | KANG S H;KIM J;STOLL M E;ABRAHAM D, SUN Y K, AMINE K .Layered Li(Ni0.5-xMn0.5-xM2x)O2(M=Co, Al, Ti;x=0, 0.025)cathode materials for Li-ion rechargeable batteries[J].Journal of Power Sources,2002,112:41-48. |
| [17] | 赵煜娟,夏定国,刘庆国.锂离子蓄电池正极材料LiNi0.85Co0.1M0.05O2的合成及性能[J].电源技术,2003(05):427-430. |
| [18] | 唐爱东,王海燕,吴晓,黄可龙.掺杂锂镍钴锰氧材料的合成及电化学性能[J].电源技术,2007(12):959-962. |
| [19] | LIM Sung-nam;AHN Wook;YEON Sun-hwa;PARK Seung-bin .Enhanced elevated-temperature performance of Li(Ni0.8Co0.15-Al0.05)O2 electrodes coated with Li2O-2B2O3 glass[J].Electrochimica Acta,2014,136:1-9. |
| [20] | 袁荣忠,瞿美臻,于作龙.锂离子电池镍系正极材料的热稳定性研究进展[J].无机材料学报,2003(05):973-979. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%