Thermal stabilities of microstructure and mechanical property have been investigated on superalloy U720Li, which is of great interest of application for jet engine and land-based turbine disc.The results showed that, the primary and secondary γ' particles maintain good thermal stability at 650 and 700℃ with aging time up to 3000 h, while the tertiary γ' is apparently dependent on aging temperature and time. The tertiary γ' particles undergo a procedure of coarsening,dissolution and eventually complete disappearance with the increasing of aging time and temperature. They exhibit unusual high sensibility upon aging temperature, which is attributed to the lattice misfit between the γ' precipitates and the matrix in the alloy. The grain boundary phase M23C6 remains stable without forming of sigma phase even with aging time up to 3000 h at 700℃. Microhardness decreases apparently with increasing aging time and aging temperature.Theoretical analysis based on dislocation mechanism indicates that the change of microhardness should be attributed to the evolution of the tertiary γ' during aging.
参考文献
| [1] | P W Keefe;S O Mancuso;G E Maurer.Superalloys 1992[J].TMS Pennsylvania,1992:487. |
| [2] | K A Green;J A Lemsky;R M Gasior.Superalloys 1996[J].TMS Pennsylvania,1996:697. |
| [3] | D J Bryant;G McIntosh.Superalloys 1996[J].TMS Pennsylvania,1996:713. |
| [4] | D Furrer;H Fecht .[J].Journal of The Minerals,Metals & Materials Society,1999,1:14. |
| [5] | D Furrer;H Fecht.Superalloys 2000[C].TMS Pennsylvania,2000:415. |
| [6] | D Helm;O Roder.[J].TMS Pennsylvania,2000:487. |
| [7] | S Bashir;M C Thomas.Superalloys 1992[J].TMS Pennsylvania,1992:747. |
| [8] | M.P.Jackson;R.C. Reed .Heat treatment of UDIMET 720Li the effect of microstructure on properties[J].Materials science and engineering,1999(1):85-97. |
| [9] | D D Furrer;H J Fecht .[J].Scripta Materialia,1999,40:1215. |
| [10] | R.C.Reed;M.P.Jackson .Characterization and modeling of the precipitation of the sigma phase in UDIMET 720 and UDIMET 720Li[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,1999(3):521-533. |
| [11] | M Maldini;V Lupinc.[M].Unpublished Paper |
| [12] | L M Brown;R K Ham.in Strengthening Mechanisms in Crystals Applied Science[M].London,1971 |
| [13] | B Reppich .[J].ACTA MATERIALIA,1982,30:95. |
| [14] | F Gabrielli;V Luinc.Strength of Metals and Alloys, ed[M].Oxford and New York,1982:607. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%