研究了草酸盐沉淀法制备超细氧化铈粉体的工艺.通过正交实验,研究了沉淀方式、沉淀剂的浓度、硝酸铈的浓度、反应温度、滴加速度等沉淀条件对氧化铈颗粒粒径的影响,找出了制备纳米氧化铈的最佳沉淀工艺条件.利用DTA/TG对氧化铈样品前驱体的热分解行为进行了分析,研究了培烧和干燥条件对氧化铈粒径和比表面积的影响,由此确立了制备氧化铈合适的焙烧和干燥条件.结果表明采用草酸盐反向沉淀法可以得到超细氧化铈粉体,其体积中心粒径D50为1.011μm、比表面积为42.69m2·g-1,晶体结构为立方晶系,CAF2萤石型结构,形状呈薄片状,分散性较好.
参考文献
| [1] | Matijevic E;Has W P .Preparation of monodispersed colloidal particles of lanthanide compounds:T.gadolinium,europium,terbium,samarium,and cerium (Ⅲ)[J].Journal of Colloid and Interface Science,1987,118:506. |
| [2] | Hirano M;Kato E .Hydrothermal synthesis of nanocrystalline cerium(Ⅳ) oxide powers[J].Journal of The American Chemical Society,1999,82(03):786. |
| [3] | Maani T;Hind H .Synthesis of cerium oxide nanoparticles by hydrothermal crystallizatian with citric acid[J].Journal of Materials Science Letters,2002,21(06):489. |
| [4] | Kuribayashi K;Uchikawa R;Akahashi K .Preparation of cerium dioxide thin films via sol-gel process and their characteristics electricalbuffer layers[J].Journal of Ceramic Society,1999,1073:275. |
| [5] | 赵新明,敖青,李胜利,孙良成.溶胶-凝胶法合成纳米铬酸锶镧的工艺研究[J].中国稀土学报,2005(02):162-165. |
| [6] | 黄剑锋,黄艳,曹丽云,贺导艳,吴建鹏,贺海燕.溶胶-凝胶法制备Sm2O3光学薄膜[J].硅酸盐学报,2006(11):1341-1344. |
| [7] | 石硬;鲁润华;汪汉卿.W/O微乳液中超细CeO2粒子的制备[J].化学通报(印刷版),1998(12):51. |
| [8] | 李伟,张莉莉,杨绪杰,陆路德,汪信.微乳液法制备超细K2Ln2Ti3O10及其光催化活性研究[J].中国稀土学报,2006(05):571-575. |
| [9] | 潘湛昌,杨文霞,张环华,肖楚民.纳米二氧化铈的电化学制备与表征[J].化工新型材料,2004(10):31-33,50. |
| [10] | 董相廷,刘桂霞,孙晶,闫景辉,洪广言.透明纳米CeO2的合成与表征[J].中国稀土学报,2002(02):123-125. |
| [11] | 徐华蕊.用喷雾反应法制备实心球形氧化铈超细粉末[J].稀土,1999(06):29. |
| [12] | 庞松,侯书恩,张涛,刘贺年.Y2O3和CeO2复合掺杂ZrO2纳米晶的制备与表征[J].中国稀土学报,2007(06):755-759. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%