The influence of double aging on the microstructure and mechanical properties of ultrahigh strength steel Aermet 100 was analyzed. Under the double aging, there is no apparent decrease in the strength of steel. However, the impact fatigue life can be prolonged by 35.5% and dynamic fracture toughness be raised by 22.6% respectively, as compared with the normal aging. Based on the observation of microscopic structure, the physical mechanism of the prolongation of impact fatigue life and the enhancement of stability of the reverted austenite, AR, is analyzed further. The results show that this new technique is a breakthrough of combination optimization between strength and toughness for Aermet 100 steel. In the light of the current understanding on this subject, the volume fracture of soften and tough AR formed in process of heat preservation at higher temperature of double aging increases drastically. Moreover, during the treatment of lower temperature of double aging, the carbon separating from the martensitic ferrite will diffuse into AR, resulting that the martensitic brittleness decreases and the stability of AR increases.
参考文献
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%