综述了合金在外加应力下的高温氧化行为,主要包括外加应力对于合金高温氧化膜生长的影响、应力对氧化膜开裂和剥落行为的影响,同时也概述了氧化膜开裂后的愈合行为研究现状.
参考文献
| [1] | 李铁藩.金属高温氧化和热腐蚀[M].北京:化学工业出版社,2003. |
| [2] | Birks N,Meier G H,Pettit F S.Introduction to the High-Temperature Oxidation of Metals[M].UK:Cambridge Press,2006. |
| [3] | 朱日彰,何业东,齐慧滨.高温腐蚀及耐高温腐蚀材料[M].上海:上海科学技术出版社,1995. |
| [4] | Nagl M M,Evans W T.The mechanical failure of oxide scales under tensile or compressive load[J].J.Mater.Sci.,1993,28:6247. |
| [5] | Evans H E.Stress effects in high temperature oxidation of metals[J].Int.Mater.Rev,1995,40(1):1. |
| [6] | 钱余海,李美栓,张亚明.力学载荷作用下合金的高温氧化行为研究状况[J]腐蚀科学与防护技术,2001,13(6):342. |
| [7] | Caplan D,Sproule G I.Effect of oxide grain structure on the high-temperature oxidation of Cr[J].Oxid.Met.,1975,9(5):459. |
| [8] | Benabderrazik G,Moulin G,et al.Influence of impurities,such as carbon and sulphur,on the high temperature oxidation behavior of Fe72Cr23A15 alloys[J].J.Mater.Sci.,1984,19:3173. |
| [9] | Douglass D L,Kofstad P,et al.International workshop on high-temperature corrosion[J].Oxid.Met.,1996,45(5/6):529. |
| [10] | Giggins C S,Pettit F S.Oxidation of Ni-Cr alloys between 800℃and 1200℃[J].Trans.RIME,1969,245:2495 |
| [11] | Hiroyuki Kawaura,Hiroshi Kawahara.New surface treatment using shot blast for improving oxidation resistance of TiAl-base alloys[J].Mater.Sci.Eng.,2002,A329-331:589. |
| [12] | Leistikow S,Wolf I,Grabke H J.Effect of cold work on the oxidation behavior and carburization resistance of alloy 800[J].Werkst.Korros.,1987,38:556. |
| [13] | Kim J M,Jeong Y H.Influence of thermomechanical treatment on the corrosion behavior of Zr-1Nb-0.2Cu alloys[J].J.Nucl.Mater.,1999,275:74. |
| [14] | Chen R Y,Yuen W Y D.Review of the high-temperature oxidation of iron and carbon steels in air or oxygen[J].Oxid.Met.,2003,59(5/6):433 |
| [15] | 金诚.应力对Ni_3A1合金氧化行为的影响[J]腐蚀科学与防护技术,1994,6(1):63 |
| [16] | 钱余海,李美栓,张亚明外加拉应力对Ti_3A1基合金500-700℃下选择氧化的影响响[J].金属学报,2003,39(9):989. |
| [17] | Ryoung Sohn,Toshio Narata.Corrosion behavior of Fe25Cr in a N2-0.1%SO2 atmosphere at 973K under mechanical loading[J].Oxid.Met.,2003,59(3/4):353. |
| [18] | Kusabiraki K,Sakuradani K,Saji S.Effects of tensile stress on grain boundary selective oxidation in an Fe36%Ni alloy[J].Tetsu-to-hagane,1998,84(4):291. |
| [19] | Gibbs G B,Hales R.Society point defect behavior and diffusional processes conference[A].Proceeding of the Conference on Vacancies[C].London:The Metals Society,1977:201-207 |
| [20] | Stroosnijder M F,Guttmann V,Gommans R J N,et al.Influence of creep deformation on the corrosion behaviour of a CeO_2 surface-modified alloy 800H in a sulphidisingoxidising-carburising environment[J].Mater.Sci.Eng.,1989,A121:581. |
| [21] | 陈永梨,黎振华,其鲁等.固体中的扩散应力研究[J]金属学报,2006,42(3):225. |
| [22] | 池田雄二,新居和嘉,引り力下にぉけるFe-C-(Al),Fe-Cr-Ni合金の高温酸化[J].日本金属学会誌,1983,47(4):191 |
| [23] | Kusabiraki K,Tsujino H,Saji S.Effects of tensile stress on the high-temperature oxidation of an Fe-38 Ni-13 Co-4.7 Nb-1.5 Ti-0ASi superalloy in air[J].ISIJ Int.,1998,38(9):1015. |
| [24] | Pieraggi B.Effect of creep or low cycle fatigue on the oxidation or hot corrosion behavior of nickel-base superalloys[J].Mater.Sci.Eng.,1987,88:199. |
| [25] | Ward G,Hockenhull B S,Hancock P.The effect of cyclic stressing on the oxidation of a low-carbon steel[J].Metall.Mater.Trans.B,1974,5(6):1451. |
| [26] | Evans H E.Spallation of oxide from stainless steel AGR nuclear fuel cladding:mechanisms and consequences[J]Mater.Sci.Technol.,1988,4(5):415. |
| [27] | Gaillet L,Viennot M,Berger P,et al.Effect of NiO scales on the creep behavior of Ni single crystals at 550℃[J].Mater.Sci.Eng.A,2002,332:382. |
| [28] | Schiitze M.Plasticity of protective oxide scales[J].Mater.Sci.Technol.,1990,6:32. |
| [29] | Evans A G,Cannon R M.Stresses in oxide films and relay tionships with cracking and spalling[J].Mater.Sci.Forum,1989,43:243. |
| [30] | Takei A,Nii K.Effect of tensile stress on the high temperature oxidation of Ni-20Cr-4Al alloy[J].Trans.Japan Inst.Met.,1984,25(8):561. |
| [31] | Grabke H J,Dennert R,Wagemann B.The effect of S,N,and C on the oxidation of Ni-20%Cr and Fe-20%Cr[J].Oxid.Met.,1997,47(5/6):495. |
| [32] | Zhang Y F.Study of oxide scale mechanical stability at elevated temperatures[D].Doctor Thesis,Crookston,University of Minnesota,1996. |
| [33] | Evans H E.Cavity formation and metallurgical changes induced by growth of oxide scale[J].Mater.Sci.Technol.,1988,4:1089. |
| [34] | Schiitze M.Mechanical properties of oxide scales[J].Oxid.Met.,1995,44(1/2):29. |
| [35] | Schutze M.Deformation and cracking behavior of protective oxide scales on heat-resistant steels under tensile strain[J].Oxid.Met.,1985,24(3/4):199. |
| [36] | Schiitze M.The healing behavior of protective oxide scales on heat-resistant steels after cracking under tensile strain[J].Oxid.Met.,1986,25(5/6):409. |
| [37] | Hancock P,Nicholis J R,Mahmood K.The influence of imposed strain rate on fracture of surface oxides[J].Corros.Sci.,1993,35(5-8):979. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%