以NH4VO3和CO( NH2)2等为起始原料,采用溶胶-凝胶法制备了V2O5微晶.研究了煅烧温度对产物物相和显微结构的影响,以及反应的合成活化能.采用X射线衍射、扫描电镜等手段对产物进行了表征.结果表明,后处理温度为500℃可得到V2O5微晶,当反应温度超过600℃时,V2O5微晶表现出(001)晶面的取向生长特征.通过差热分析,计算得到其合成活化能为95.81 kJ/mol.
参考文献
| [1] | 甄恩明,徐刚,苗蕾,徐雪青.溶胶-凝胶法制备高c轴取向纳米V2O5薄膜[J].微纳电子技术,2009(09):530-534,539. |
| [2] | 王玉泉 .钒氧化物纳米材料的制备和性能[D].北京:清华大学,2008. |
| [3] | Z.J. Lao;K. Konstantinov;Y. Tournaire .Synthesis of vanadium pentoxide powders with enhanced surface-area for electrochemical capacitors[J].Journal of Power Sources,2006(2):1451-1454. |
| [4] | Huang C M;Liu X Q;Keng L B et al.Hydrothermal Synthesis of Vanadium Oxide Nanotuhes by a Facile Route[J].Rare Metals,2006,25:88-93. |
| [5] | Alzueta M U;Bilbao R;Millera A et al.Impact of New Findings Concerning Urea Thermal Decomposition on the Modeling of the Urea-SNCRProcess[J].Energy &Fnels,2000,14(02):509-510. |
| [6] | 吴刚.材料结构表征及应用[M].北京:化学工业出版社,2002:270-271. |
| [7] | SU Qing,PAN Xiaojun,XIE Erqing,WANG Yinyue,QIU Jiawen,LIU Xueqin.Influence of temperature on the microstructure of V2O5 film prepared by DC magnetron sputtering[J].稀有金属（英文版）,2006(z1):82-87. |
| [8] | 翁臻培.结晶学[M].北京:中国建筑工业出版社,1986:22-23. |
| [9] | Hanreld J;Wong H P et al.Synlhesis and Properties of Polypyrrole-Vanadium Oxide Hybrid Aerogels[J].Journal of Non-Crystal Sdids,1998,225:319-324. |
| [10] | 周静,陈文,徐庆,闵新民.V2O5复合薄膜材料的电子结构研究[J].硅酸盐学报,2002(02):208-211,215. |
| [11] | 王惠,罗瑞盈,杨延清,翟高红,冉新权,文振翼.一种碳前驱物热解反应的热力学和动力学研究[J].材料研究学报,2001(02):159-165. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%