The mathematics model for temperature field of water-cooling copper crucible induction skull melting process was established. The program for simulating temperature field of melting process was developed with finite element method. The temperature field of the melting process for Ti-47Al-2Cr-2Nb alloy was calculated. During melting period, the temperature is raised gradually along radius augmentation direction. The elements of the charge near the crucible wall are molten first. The center elements of the charge are molten last. The melting time of the center element is just that of all the charge melting. The melting time of Ti-47Al-2Cr-2Nb alloy is 15min. In which, the charge was heated by low power 80kW for 9min and by high power 300kW for 6min. When melting Ti-47Al-2Cr-2Nb alloy,the loading power is nearly direct proportion to melt temperature. Increasing loading power may raise melt temperature. The best melting power of Ti-47Al-2Cr-2Nb alloy is 305-310kW. This is identical with the melting test and has guidance sense to the melting process of actual titanium alloy.
参考文献
| [1] | R C Rodgers.[J].Foundry,1991:58. |
| [2] | J K Choi;C P Hong.[J].Cast Metals:226. |
| [3] | H G Fjaer;A M Alspen.[J].Metallurgical and Materials Transactions:1049. |
| [4] | J Q Wang;S F Hansen;P N Hansen.Modeling of Casting and Welding Process IV,eds.A.F.Giamei and G.J.Abbaschian[C].TMS,1988:741. |
| [5] | P Jonsson .[Z].A FS Trans |
| [6] | R A Stoehr;C Wang .[Z].A FS Trans |
| [7] | Z Y Chen .Post Doctor Report of Institute of Metal Research[R].The Chinese Academy of Sciences Shenyang,2001. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%