采用粉末冶金方法制备了添加质量分数为69%二硫化钼的镍铬基复合材料;对其在800,900和950℃的高温氧化行为进行了研究,绘制了氧化动力学曲线;用扫描电镜对其氧化表面形貌和横截面组织进行了观察.结果表明:该镍铬基复合材料在800℃以及900℃氧化100 h后,其氧化动力学符合抛物线规律,在材料表面生成了Cr2O3和NiCr2O4氧化膜,具有一定的抗氧化性能;在950℃氧化时,表面氧化膜出现剥落.
参考文献
| [1] | 姚素薇,姚颖悟,张卫国,王宏智,赵越.Ni-W/ZrO2纳米复合镀层耐高温氧化性能分析[J].天津大学学报,2007(03):308-311. |
| [2] | 黄志伟,袁福河,王中光,朱世杰,王富岗.铸造镍基高温合金M963的高温低周疲劳行为[J].金属学报,2007(07):678-682. |
| [3] | Wang CJ;Chen SM .Microstructure and cyclic oxidation behavior of hot dip aluminized coating on Ni-base superalloy Inconel 718[J].Surface & Coatings Technology,2006(7):3862-3866. |
| [4] | Singh H;Puri D;Prakash S;Maiti R .Characterization of oxide scales to evaluate high temperature oxidation behavior of Ni-20Cr coated superalloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(1-2):110-116. |
| [5] | Xiong DS. .Lubrication behavior of Ni-Cr-based alloys containing MoS2 at high temperature[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2001(2):1094-1099. |
| [6] | 薛茂权,黄之德.MoS2对镍基复合材料力学性能的影响[J].机械研究与应用,2007(01):38-39. |
| [7] | 杨世伟,娄瑾,姜艳,刘海涛.K4104镍基高温合金渗Al-Si涂层氧化动力学[J].材料热处理学报,2006(01):108-111. |
| [8] | 李云,徐宁,郭建亭,袁超,杨洪才.镍基铸造高温合金K52在900℃恒温氧化性能的研究[J].高等学校化学学报,2007(01):113-116. |
| [9] | 李云,袁超,郭建亭,杨洪才.铸造镍基高温合金K35的氧化动力学[J].东北大学学报(自然科学版),2003(01):75-78. |
| [10] | 胡传顺,王福会,吴维.电子束表面熔凝处理对镍基高温合金熔凝层组织及其抗高温氧化性能的影响[J].金属热处理,2001(07):20-22. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%