依据钛合金相关设计理论设计了低弹性模量、中高强度、良好塑性的新型生物医用近β型Ti35Nb3．7Zr1．3Mo合金，研究了固溶温度和时效温度对合金组织和力学性能的影响。结果表明：随着固溶温度的升高，α相逐渐溶解，合金的强度和弹性模量尚未发生明显变化。在低温时效时析出脆性ω相；随着时效温度升高，逐渐析出α相，且α相逐渐粗化；合金的强度与弹性模量先升高，达到峰值后下降；延伸率先降低后升高。合金经750℃固溶和450℃时效后综合力学性能优良，可以满足生物植入材料力学性能的要求。
A new β-type alloy Ti35Nb3. 7Zr1. 3Mo for biomedical implant with low Young′s modulus, high tensile strength and good plasticity was designed based on related design theory of titanium alloy. The influence of solid solution and aging temperature on microstructures and mechanical properties were investigated. It was found that α phase was dissolved in β matrix gradually with the increasing of solution temperature and the strength and elastic modulus have no significant change. The ω phase precipitates when aged at low temperature, while α phase precipitates and becomes coarse gradually when the aging temperature increases. With the increasing of aging temperature, the strength and Young′s modulus of the alloy increase first to the peak and then decrease, while the elongation of the alloy decreases first and then increases. The alloy processed by 750 ℃ × 30 min solution treatment and 450 ℃ × 12 h aging possesses excellent integrated mechanical properties and can meet the requirement for the mechanical properties of implant materials.
参考文献
| [1] | NIINOMI M .Recent research and development in titanium alloys for biomedical applications and healthcare goods[J].Science and Technology of Advanced Materials,2003,243 |
| [2] | WANG K.The use of titanium for medical applications in the USA [J]. Materials Science and Engineering, 1996, A213:134-137.,1996. |
| [3] | KURODAD,NIINOMIM,MORINAGAM,et al. Design and mechanical properties of new type titanium alloys for implant materials A [J]. Materials Science and Engineering,1998, 243:244-249.,1998. |
| [4] | 浦素云.金属植入材料及腐蚀[M].北京:北京航空航天大学出版社, 1990. PU Suyun.Metal implant materials and corrosion [M]. Beijing:Beijing University of Aeronautics and Astronautics Press, 1990.,1990. |
| [5] | VANNR .Titanium:the implant material of today[J].,1987,22 |
| [6] | SAITOT,FURUTAT,HWANGJH,etal .Multifunc-tional Alloys Obtained via a Dislocation-Free Plastic De-formation Mechanism[J].Science,2003,300 |
| [7] | MOFFTADL,LARBALESTIERDC.The composition between martensite and omega in quenched Ti-Nb alloys [J].Metallurgy Transcations,1998, 19A:1677-1686.,1998. |
| [8] | QAZIJI,MARQUARDTB,ALLARDLF,et al. Phase transformations in Ti-35Nb-7Zr-5Ta-(0.06~0.68)O alloys[J].Materials Science and Engineering C,2005, 25:389-397.,2005. |
| [9] | YANOT,MURAKAMIY,SHINDOD,et al .Trans-mission electron microscopy studies on nanometer-sizedωphase produced in Gum Metal[J].Scripta Ma-terialia,2010,63 |
| [10] | CUI W F, GUO A H. Microstructures and properties of biomedical TiNbZrFeβ-titanium alloy under ageing conditions[J]. Materials Science and Engineering A, 2009, 527:258-262.,2009. |
| [11] | NG H P, DOUGUET E, BETTLES C J, et al. Age-hardening behaviour of two metastable beta-titanium alloys[J]. Materials Science and Engineering A,2010, 527:7017-7026.,2010. |
| [12] | GLORIANT T, TEXIER G, SUN F, et al. Character-ization of nanophase precipitation in a metastableβtita-nium-based alloy by electrical resistivity, dilatometry and neutron diffraction[J]. Scripta Materialia,2008, 58:271-274.,2008. |
| [13] | 顾桂月,陈锋,张强,余新泉.热处理对Ti30Nb5Ta6Zr合金组织和力学性能的影响[J].稀有金属材料与工程,2010(04):678-681. |
| [14] | TANG X, AHMED T, RACK H J . Phase transforma-tions in Ti-Nb-Zr and Ti-Nb-Ta-Zr alloys[J].Ma-terials Science,2000,35 |
| [15] | 张喜燕,赵永庆,白晨光.钛合金及应用[M].北京:化学工业出版社,2005. ZHANG Xiyan, ZHAO Yongqing, BA Chenguang. Titanium alloy and its application [M]. Beijing:Chemical Industry Press, 2005.,2005. |
| [16] | PALADUGU M, KENT D, CUI W, et al. Strengthe-ning of cast Ti-25Nb-3Mo-2Zr-2Sn alloy through precipition ofα in two discrete crystallographic orienta-tions. Materials Science and Engineering A [J]. 2010, 527:6601-6606.,2010. |
| [17] | TAHARA M, HEE Y K, HOSODA H, et al. Effect of Nitrogen addition and annealing temperature on superelastic properties of Ti-Nb-Zr-Ta alloys. Materials Science and Engineering A [J]. 2010, 527:644-652.,2010. |
| [18] | BOCCACCINI, ALDO R. Young ’ s modulus of cast-iron as a function of volume content, shape and orientation of graphite inclusions [J]. Z Metallkd, 1997,V88:23-26.,1997. |
| [19] | YAO Q, XING H, GUO W Y, et al. First-Principle Calculation of Phase Stability and Elastic Property ofα" and β in Ti-25 at%Nb Alloy. Rare Metals and Materials and Engineering. 2009,38:663-666.,2009. |
| [20] | CHANG Lizhao. Mechanical and electrochemical charac-terization of Ti-12Mo-5Zr alloy for biomedical applica-tion. Journal of Alloys Compound. 2008,466:535-542.,2008. |
| [21] | ZHOU Y L, NIINOMI M, AKAHORI T. Effects of Ta content on Young′s modulus and tensile properties of binary Ti-Ta alloys for biomedical applications. Material Science and Engineering A,2004, 371:283-290.,2004. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%