采用维氏(HV)硬度测试、力学性能测试、透射电镜(TEM)观察等技术手段,研究了双级时效工艺对2099合金组织性能的影响.结果显示,双级时效处理能够显著改善2099合金的综合力学性能指标,合金屈服强度和抗拉强度的增幅分别达144 MPa和98 MPa,而塑性降低0.6％.终时效温度由146℃升高到170 ℃,达到峰时效态的时间缩短24 h,综合强塑性指标波动较小.时效过程中析出相的演化规律为:预时效态,基体析出相以δ'相为主,T1相较少;峰时效态,以T1相为主,δ'相次之,θ'相很少;过时效态,T1相和δ'相略有粗化,且δ'相数量减少.
参考文献
| [1] | James Fragomeni;Robert Wheeler;K.V. Jata.Effect of Single and Duplex Aging on Precipitation Response, Microstructure, and Fatigue Crack Behavior in Al-Li-Cu Alloy AF/C-458[J].Journal of Materials Engineering and Performance,20051(1):18-27. |
| [2] | H. Babel;J. Gibson;M. Tarkanian;C. Parrish;M. Prietto;A. Ordonez-Chu;H. Haberl;J. Kabisch;R. Clark;J. Ogren;O. S. Es Said.2099 Aluminum-Lithium with Key-Locked Inserts for Aerospace Applications[J].Journal of Materials Engineering and Performance,20075(5):584-591. |
| [3] | Fei Zhang;Jian Shen;Xiao-Dong Yan;Jian-Lin Sun;Xiao-Long Sun;Yin Yang.Homogenization heat treatment of 2099 Al-Li alloy[J].稀有金属（英文版）,2014(1):28-36. |
| [4] | J. Jabra;M. Romios;J. Lai.The Effect of Thermal Exposure on the Mechanical Properties of 2099-T6 Die Forgings, 2099-T83 Extrusions, 7075-T7651 Plate, 7085-T7452 Die Forgings, 7085-T7651 Plate, and 2397-T87 Plate Aluminum Alloys[J].Journal of Materials Engineering and Performance,20065(5):601-607. |
| [5] | D.C.V.Kooi;W.Park.Characterization of cryogenic mechanical properties of aluminum-lithium alloy C-458[J].Scripta materialia,199911(11):1185-1190. |
| [6] | 魏修宇;郑子樵;佘玲娟;陈秋妮;李世晨.Mg、Zn在2099铝锂合金中的微合金化作用[J].稀有金属材料与工程,2010(9):1583-1587. |
| [7] | 朱小辉;郑子樵;钟申.Mg和Zn对2099合金时效组织与拉伸性能的影响[J].中国有色金属学报,2010(10):1861-1867. |
| [8] | 林毅;郑子樵;李世晨;孔祥;韩烨.2099铝锂合金微观组织及性能[J].中国有色金属学报,2013(7):1848-1854. |
| [9] | 张飞;沈健;闫晓东;孙建林;饶茂;胡兴华.2099合金挤压极限图的构建及验证[J].稀有金属材料与工程,2014(2):403-407. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%