A Zinc coating containing CeO2 nanoparticles has been deposited by electrodeposition in a zinc plating bath.The content of CeO2 in the coating is 0.22 mass%. The results of weight loss experiments and electrochemistry tests show that corrosion resistance of the Zinc coating containing CeO2 nanoparticles is remarkably improved in contrast to the pure zinc coating in 0.5 M MgSO4 solution. The effects of CeO2 microparticles on the corrosion resistance of the zinc coating have been studied, the results show that CeO2 microparticles have no effect on the corrosion resistance of the zinc coating. SEM and XRD experiments suggest that the presence of CeO2 nanoparticles in the coating causes the modification of the surface morphology and preferential orientation of the crystal planes; therefore, the reason for the enhancement of corrosion resistance is mainly related to improvement of the structure of the coating.
参考文献
| [1] | Zhenmi T U .Characteristic, Applications and Developments of Electroplated Zn Alloy Deposits[J].Materials Protection,2000,33(01):37-42. |
| [2] | Kalantary M R .Zinc Alloy Electrodeposition for Corrosion Protection[J].Plating and Surface Finishing,1994,81(06):80-88. |
| [3] | Narasimhamurthy V;Sheshadri B S .Electrodeposition of ZincIron Alloy from an Acid Sulfate Bath Containing Triethanolamine[J].Metal Finishing,1997,95(09):44-47. |
| [4] | Li S J;He J P;Sun L .The Effect of Rare earths on corrosion Resistance of Zinc coating by Electrodeposition[J].Materials Protection,1991,24(03):4-6. |
| [5] | Mehmood M;Zhang B P;Akiyama E et al.Experimental Evidence for the Critical Size of Heterogeneity Areas for Pitting Corrosion of Cr-Zr Alloys in 6M HCl[J].Corrosion Science,1998,40:1-17. |
| [6] | Li Ying;Wang F H;Liu G .Grian-Size Effect on The electrochemical Corrosion of Surface Nanocrystallized Low Carbon Steel[J].Journal Chinese Society for Corrosion and Protection,2001,21(04):215-219. |
| [7] | 马美华,李峰,李小华,潘涛,忻新泉.镍-磷-锌盐纳米复合化学镀层抗腐蚀性能的研究[J].应用化学,2001(07):509-512. |
| [8] | ZhuLQ;Li W P;Zhong Q P .Effect ofZrO2 Particles in the Electrodeposited Ni-W-B Amorphous Composite Coatings[J].Materials for Mechanical Engineering,1998,22:9-11,27. |
| [9] | B. BOZZINI;P. L. CAVALLOTTI;G. PARISI .Corrosion and erosion-corrosion of electrodeposited Ni-P/B_4 C composites[J].British Corrosion Journal,2001(1):49-55. |
| [10] | Ye G C;Lee D N .Orientation and Microstructure of Dull Nickel Electrodeposits[J].Plating and Surface Finishing,1981,68(04):60-64. |
| [11] | 肖理生,于化龙.Effect of Cerium on Corrosion Resistance of Bright Zinc Electrodeposit[J].JOURNAL OF RARE EARTHS,1994(01):18. |
| [12] | HeJP;LiS J;ChenWH .Effect of Cerium element on Structure and Properties of Electrodeposited Zinc Coatings[J].Corrosion and Protection,1994,15(05):247-249. |
| [13] | Lidia Benea;Pier Luigi Bonora;Alberto Borello .Composite Electrodeposition to Obtain Nanostructured Coatings[J].Journal of the Electrochemical Society,2001(7):C461-C465. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%