通过连续渗流方法制备出钨丝体积分数为62％～66％,钨丝直径分别为40,60,80,150 μm的钨丝增强锆基非晶合金复合材料.研究表明,钨丝直径为80 μm时,非晶合金复合材料的抗拉伸强度和延伸率分别达到最大值,当钨丝直径增加到150 μm时,非晶复合材料的抗拉伸强度和塑性急剧降低.对断U形貌进行了分析.研究发现钨丝增强非晶复合材料中,增强相直径不同引起面体率变化,从而影响非晶和钨丝界面的应力、钨丝在三轴应力状态下的变形和断裂以及非晶基体中剪切带的形成和扩展,最终影响复合材料的拉伸力学性能.
参考文献
| [1] | Schuh CA;Hufnagel TC;Ramamurty U .Overview No.144 - Mechanical behavior of amorphous alloys[J].Acta materialia,2007(12):4067-4109. |
| [2] | 孙剑飞,黄永江,邢大伟,颜鑫,王刚,沈军.Zr-Cu-Ni-Ta-Al块体非晶合金复合材料的合成及力学性能[J].稀有金属材料与工程,2007(07):1153-1156. |
| [3] | 沈军,高玉来,孙剑飞,陈德民,王刚,邢大伟,周彼德.Zr-Ti-Cu-Ni-Be大块非晶合金等温晶化过程相分离研究[J].稀有金属材料与工程,2004(12):1257-1260. |
| [4] | Rong, G.;Huang, D.W.;Yang, M.C..Penetrating behaviors of Zr-based metallic glass composite rods reinforced by tungsten fibers[J].Theoretical and Applied Fracture Mechanics,2012:21-27. |
| [5] | Wang ML;Hui X;Chen GL .Interfacial characteristics and mechanical properties of a modified Nb-containing Zr-based bulk metallic glass composite reinforced with W fiber[J].Journal of Materials Research,2008(2):320-327. |
| [6] | 王美玲,惠希东,寇宏超,陈国良.钨丝/Zr基金属玻璃复合材料的界面反应与扩散[J].稀有金属材料与工程,2005(07):1102-1105. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%