In order to explore the behavior laws of sinter reduction in TGR-OBF (top gas recycling-oxygen blast furnace), reduction experiments of sinter have been conducted by thermal balance mass loss method with different atmospheres, temperatures and volume flows. The changes of RI (reduction degree of Fe2O3), RI′ (reduction rate of Fe2O3) and r (reduction degree of FeO) have been examined. The results show that the reduction of sinter was significantly improved under TGR-OBF atmosphere, and the RI and r were measured up to 98.2% and 97.8% at 900 ℃ respectively. With increasing of the reduction temperature, the reduction of sinter speeded up greatly, and the reduction time-duration shortened from 117 min at 900 ℃ to 63 min at 1100 ℃. Moreover, the reduction of sinter enhanced with increasing of the reductive gas flow. When the flow increased from 10 to 15 L/min, the initial reduction rate of sinter increased from 2.47%/min to 3.73%/min. While increasing H2 and CO contents in the reductive atmosphere, the reduction of sinter was promoted. Besides, H2 influenced more evidently than CO to the reduction of sinter, especially in the later stage of the reduction process, for instance, the reduction of wustite will be improved enormously when increasing the H2 content in the reductive atmosphere.
参考文献
| [1] | |
| [2] | Qin Minsheng, Gao Zhengkai, Wang Guanlun et al. Study on Blast Furnace Operation with all Oxygen Blast [J]. IRON AND STEEL,1987,22(12):1～7.[2] Hideyuki YAMAOKA, Yasuo KAMEI. Experimental Study on an Oxygen Blast Furnace Process Using a Small Test Plant [J]. ISIJ International, 1992, 32(6): 709～7l5.[3] Zhang J L. The Applied and Fundamental Research on Nitrogen Free Blast Furnace [D] ∥ Beijing: University of Science and Technology Beijing, 2000.[4] Qin Minsheng, Zhang Jianliang, Qi Baoming et al. Advantage of Smelting Vanadium-Titanium Magnetite Ore with all Oxygen Blast [J]. Iron Steel Vanadium Titanium. 1991,12(2): 1～6.[5] Yin J W, Kuang C J, Gao Z K, et al. Pilot Experiment of Filtration System of Blast Furnace Hot Gas [J]. Journal of University of Science and Technology Beijing. 2002, 24(1):19.[6] Hannu HELLE, Mikko HELLE, Frank PETTERSSON and Henrik SAXéN. Multi-objective Optimization of Ironmaking in the Blast Furnace with Top Gas Recycling [J]. ISIJ International, 2010, 50(10): 1380～1387.[7] Hannu HELLE, Mikko HELLE, Henrik SAXéN and Frank PETTERSSON. Optimization of Top Gas Recycling Conditions under High Oxygen Enrichment in the Blast Furnace [J].ISIJ International,2010，50(7): 931～938.[8] ZHANG Hui, LI HuiQuan, TANG Qing & BAO WeiJun.Conceptual Design and Simulation Analysis of Thermal Behaviors of TGR Blast Furnace and Oxygen Blast Furnace [J]. SCIENCE CHINA Technological Sciences.2010,53(1):85～92.[9] Guangqing Zuo and Alexandra Hirsch. The Trial of the Top Gas Recycling Blast Furnace at LKAB's EBF and Scale-up [C] ∥ Proceedings of the 4th Ulcos seminar. Essen: 2008.[10] Gérard Danloy, Jan van der Stel, Peter Schm?le.Heat and Mass Balances in the ULCOS Blast Furnace [C] ∥ Proceedings of the 4th Ulcos seminar. Essen: 2008.[11] Joachim Hülstrung.Raceway Modelling in the ULCOS Blast Furnace [C] ∥ Proceedings of the 4th Ulcos seminar. Essen: 2008..[12] Huang X H. The Principle of Ferrous Metallurgy[M]. Beijing: Metallurgical Industry Press, 2007: 284～288.[13] Raymond Longbottom and Leiv Kolbeinsen .Iron ore Reduction with CO and H2 Gas Mixtures -Thermodynamic and Kinetic Modelling [C] ∥ Proceedings of the 4th Ulcos seminar. Essen: 2008.[14] Elsayed A. MOUSA, Alexander BABICH and Dieter SENK. Effect of Nut Coke-sinter Mixture on the Blast Furnace Performance [J]. ISIJ International，2011，51(3)：350～358. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%