The effects of Fe2O3 addition in MgO-CaO refractory on desulfurization of liquid iron were studied by SEM, EDA and chemical analysis. Fe2O3 of 1 % and 4 % were added to MgO-CaO refractory as the lining of graphite crucible in which 150 g iron powder with sulfur of 0.15 % was charged. It is found that when the sample is heated at 1 600 ℃ for 40 min, 60 min and 90 min, the addition with Fe2O3 of 1 % improves desulfurization greatly. However, the desulfurization ratio of the refractory with Fe2O3 addition of 4 % is less than that with Fe2O3 addition of 1 %. For the soaking time of 90 min, the desulfurization ratio is less than those of 40 min and 60 min. These phenomena were explained by the contrary roles of O2- and Fe2+ formed by reaction between liquid iron and Fe2O3 on desulfurization.
参考文献
| [1] | Ludlow V;Watkinson H;Bain K G.Role of Tundish Powder in Tundish Metallurgy[M].Germany: Verein Deut-scher Eisenhuttenleute,1994 |
| [2] | Sasai K;Mizukami Y .Effect of Tundish Cover Powder and Teeming Stream on Oxidation Rate of Molten Steel in Tundish[J].ISIJ International,1998,38(04):332-338. |
| [3] | Li Nan.Thinking about Some Problems Related to Refractory for the New Century[J].Refractory Application,2001(1-2) |
| [4] | Chen Xiang-wu.Deoxidization in Steelmaking[M].北京:冶金工业出版社,1989 |
| [5] | 李楠,匡加才.碱性耐火材料脱磷作用的研究[J].耐火材料,2000(05):249-251. |
| [6] | Wei Yao-wu;Li Nan.Desulfurizaiton of MgO-CaO Refracto-ries on Molten Iron[A].Cancun,Mexico,2001:183-188. |
| [7] | Uchida S;Dagawa T;Ototani .Effect of Various Oxide Ac-tives in CaO-MgO Refractories on Desulfurization Behavior of Molten Iron[J].interceram,1991,40(05):290-294. |
| [8] | Degawa T.Recent Development of High Purify Advanced Metals and Alloys Using Calcia Refining Process[M].北京:冶金工业出版社,1991 |
| [9] | Pegawa T;Vohida S;Ototani T.Development of CaO-MgO Refractories and Their Effects on Refined Mechanism of Ex-tremely Clean Steel[A].To-kyo,Japan,1987:842-847. |
| [10] | Huang Xi-hu.Metallurgy Theory of Iron and Steelmaking[M].北京:冶金工业出版社,1997 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%