利用维氏硬度和拉伸力学性能测试、Kahn撕裂试验等方法,研究二次时效对7055铝合金力学性能的影响.结果表明,经过120℃,150℃和180℃高温欠时效,甚至峰值时效处理后,再进行60℃和100℃低温二次时效,可以获得超过相应单级峰值时效的硬度和强度.Kahn撕裂试验表明,二次时效温度从60℃提高到100℃,可以缩短二次峰值硬化时间,但不利于7055铝合金断裂韧性的改善.在相同预时效温度下,缩短预时效时间比峰值时效状态更有利于断裂韧性的改善.较低预时效和二次时效温度以及较短预时效时间有利于获得强度和断裂韧性的良好配合.
参考文献
| [1] | Lynch S P .[J].Materials Science and Engineering A,1991,36:25. |
| [2] | Pitcher P D;Stewart R T;Gupta S .[J].Scripta Metallurgica et Materialia,1992,26:511. |
| [3] | Kerr M J;Sweet E D;Bennett C G;Muddle B C .[J].Materials Science Forum,1996,217～222:107. |
| [4] | Lumley R N;Morton A J;Polmear I J .[J].Acta Materialia,2002,50:3597. |
| [5] | Lumley R N;Polmear I J;Morton A J .International Patent[P].Application PCT/AU00/01601,2002. |
| [6] | Lumley R N;Polmear I J;Morton A J .International Patent[P].Application PCT/AU02/00234,2002. |
| [7] | Kaufman J G;Hunsicker Y.Fracture Toughness Testing[M].New York:ALCOA Research Laboratories,1991:209. |
| [8] | Dumont D.;Deschamps A.;Brechet Y. .On the relationship between microstructure, strength and toughness in AA7050 aluminum alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):326-336. |
| [9] | Lumley R N;Polmear I J;Morton A J .[J].Materials Science Forum,2003,426/432:303. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%