用硅青铜(QSi3-1)电极,分别在硅油和氩气中对Ti17钛合金进行了电火花表面强化.利用扫描电镜、X射线衍射仪、辉光放电光谱仪、显微硬度计和MM200磨损试验机等对强化层的成分、组织、硬度和耐磨性进行了研究.结果表明,用QSi3-1电极在氩气和硅油中于30V、1500μF的电参数下.分别可获得显微硬度高达HV550和HV494、厚度约10μm和5μm的强化层;前者所得强化层以Ci3Cu、Cu为主,同时还有少量的TiSi2和Ti;后者所得强化层由Ti3Cu和Cu相及少量TiO、Ti2N、Ti3SiC2相组成;在试样转速为200r/min,干圆环摩擦磨损条件下、在氩气和硅油中强化试样的磨损量仅为钛合金基体的1/56和1/24.钛合金基体主要以氧化磨损和粘着磨损为主;表面改性层磨损的原因则与强化层脱落造成磨粒磨损有关.
参考文献
| [1] | Donachie M J.Titanium-A technical guide,ASM International[M].New York:The Materials Information Society,2000 |
| [2] | Bill R C .Selected fretting wear-resistance coatings for BT9 Alloy[J].Wear,1985,106:283-301. |
| [3] | T. Wierzchon .Surface Engineering of Titanium Alloys: New Prospective Applications[J].Materials Science Forum,2003(Pt.3):2563-2568. |
| [4] | Pang W;Man HC;Yue TM .Laser surface coating of Mo-WC metal matrix composite on Ti6A14V alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):144-153. |
| [5] | Lima MSF;Folio F;Mischler S .Microstructure and surface properties of laser-remelted titanium nitride coatings on titanium[J].Surface & Coatings Technology,2005(1):83-91. |
| [6] | 陈钟燮.电火花表面强化工[M].北京:机械工业出版社,1987 |
| [7] | 乔生儒,韩栋,李玫.钢铁表面电火花淬火组织超细化及机理[J].机械工程材料,2004(08):7-9. |
| [8] | H. G. Lee;J. Simao;D. K. Aspinwall .Electrical discharge surface alloying[J].Journal of Materials Processing Technology,2004(1/3):334-340. |
| [9] | Allen E B;Gary L;Sheldon A E .A parametric study of improving tool life by electrospark deposition[J].Wear,1990,138:137-151. |
| [10] | 孙希泰.材料表面强化技术[M].北京:化学工业出版社,2005 |
| [11] | 汪瑞军,钱乙余,黄小鸥,刘军.TC1合金表面电火花沉积WC-8Co涂层界面行为[J].焊接学报,2003(05):88-90,96. |
| [12] | 朱健,张全忠,张立文,王德新,王伟,陈文华,刘丹.钛合金表面电火花沉积WC涂层的研究[J].金属热处理,2005(02):11-14. |
| [13] | 王金友;葛志明;周彦邦.航空用钛合金[M].上海:上海科学技术出版社,1985 |
| [14] | 李建明.磨损金属学[M].北京:冶金工业出版社,1990 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%