Hot Deformation Behavior of an As-cast Duplex Stainless Steel

材料科学技术（英文）, 2003, 19(4): 379-381.

^1, , ^2, , ^3,

1.Institute of Metal Research, Chinese Academy of Sciences, Shengyang 110016, China;School of Metal Material, Shenyang University of Technology, Shengyang 110023, China

2.Institute of Metal Research, Chinese Academy of Sciences, Shengyang 110016, China

3.Institute of Metal Research, Chinese Academy of Sciences, Shengyang 110016, China

Hot Deformation Behavior of an As-cast Duplex Stainless Steel

Keywords： Hot deformation

The hot deformation behavior of an as-cast 0Cr17Mn14Mo2N duplex stainless steel has been studied by hot compression test at the temperature range from 1000℃ to 1200℃, and the strain rates are 0.1 s-1, 1 s-1 and 5 s-1,respectively. It was found that during hot deformation there is only dynamic recovery taking place within the δ-ferrite phase, but the γ-austenite phase undergoes dynamic recrystallization. The activation energy of the steel for hot compression is estimated to be 480 k J/mol.

参考文献

[1]	N D Ryan;H J McQueen .[J].Journal of Jonas:Can Celall Quart,1990,29(02):147.
[2]	W Gao;A Belyakov .[J].Journal of Miura and T Sakai:Mater Sci Eng,1999,A265:233.
[3]	K. TSUZAKI;HUANG XIAOXU;T. MAKI .MECHANISM OF DYNAMIC CONTINUOUS RECRYSTALLIZATION DURING SUPERPLASTIC DEFORMATION IN A MICRODUPLEX STAINLESS STEEL[J].Acta materialia,1996(11):4491-4499.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Hot Deformation Behavior of an As-cast Duplex Stainless Steel

参考文献