采用慢应变速率拉伸试验研究了16MnR钢在碳酸盐和硫化氢复杂环境中的应力腐蚀开裂敏感性.结果表明,在含碳酸盐和硫化氢的复杂介质环境中,16MnR钢的应力腐蚀敏感性指数低于25%;温度由常温升高至57.5℃时,16MnR钢母材与热影响区的应力腐蚀敏感性略有升高,碳酸盐和硫化氢浓度对16MnR钢在此复杂环境中的应力腐蚀敏感性存在相互影响.
By means of slow strain rate test（SSRT）,the stress corrosion cracking（SCC） susceptibility of 16MnR in complex environment containing carbonate and hydrogen sulfide were investigated.In this environment,the stress corrosion cracking susceptibility indexes of 16MnR were lower than 25%.With the temperature increasing from 25℃to 57.5℃,the stress corrosion cracking susceptibility indexes increased slightly,and the concentration of hydrogen sulfide and the carbonate affected the susceptibility reciprocally.
参考文献
| [1] | 宋光雄,张晓庆,常炎衍等.压力设备腐蚀失效案例统计分析[J].材料工程,2004,2:6. |
| [2] | 余存烨.石油设备腐蚀开裂的回顾与思考[J].石油化工腐蚀与防护,2006,23(2):19. |
| [3] | 郑文龙,于青.钢的环境敏感断裂[M].北京:化学工业出版社,1988. |
| [4] | 乔利杰,王燕斌,褚武扬.应力腐蚀机理[M].北京:科学出版社,1993. |
| [5] | 董绍平,袁军国.16MnR、316L钢在高含硫原油中的腐蚀性研究[J].压力容器,2002,19(3):12. |
| [6] | 何伟,陈进伟.炼油工业中腐蚀研究的进展[J].石油化工腐蚀与防护,1997,14(2):8. |
| [7] | 刘富胜,许春磊,方德明.16MnR钢在含H2S介质中的慢应变速率腐蚀试验研究[J].腐蚀科学与防护技术,2007,19(2):131. |
| [8] | 卢志明,童水光,方德明等.16MnR钢在含H2S介质中慢拉伸应力腐蚀试验研究[J].化工机械,2001,28(3):140. |
| [9] | 胡钢,许淳淳,池琳等.X70管线钢在HCO3^-/CO3^2-溶液中的电化学行为研究[J].腐蚀科学与防护技术,2005,17(5):331. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%