通过显微硬度测试、拉伸试验、能谱分析、SEM及TEM观察,研究了少量Ag对低Cu/Mg比的Al-Mg-Cu-Li合金微观组织与性能的影响.实验结果表明:Ag的添加提高了该合金的硬度和强度,同时改善了其塑性,并延缓了过时效的发生.微观组织观察表明:Ag的添加促进Z相的均匀弥散析出,同时抑制了s'相在缺陷处非均匀析出;并且Ag的添加还促使了时效初期合金中δ'相的细化和弥散分布,延缓了δ'相的长大.同时分析了析出相种类对合金塑性的影响.
参考文献
| [1] | Brook G B.Precipitation in Metals,Spec Rep No.3[M].UK:Fulmer Res Inst,UK,1963 |
| [2] | Kerry S;Scott V D .[J].Metal Science Journal,1984,18:289. |
| [3] | Chopra H D;Liu K J;Muddle B C et al.[J].Philosophical Magazine Letters,1995,71:319. |
| [4] | Itoh G;Cui Q;Kanno M .[J].Materials Science and Engineering,1996,A211:128. |
| [5] | Chopra H D;Muddle B C;Polmear I J .[J].Philosophical Magazine Letters,1996,73:351. |
| [6] | Ringer S P;Quan G C;Sakurai T .[J].Materials Science and Engineering,1998,A250:120. |
| [7] | Radmiloviv V;Thomas G .[J].Scripta Metallurgica et Materialia,1989,23:1141. |
| [8] | Vietz J T;Saragant K R;Polmear I J .[J].Journal of the Institute of Metals,1964,92:327. |
| [9] | Nie J F;Muddle B C .[J].Materials Science Forum,1996,217-222:1257. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%