利用摩尔比为NaCl:KCl:NaF=2:2:1的碱金属卤化物混合体系做载体,等摩尔比的Na2SiF6和Si粉作渗硅剂,在900 ℃下利用熔融盐法对0Cr18Ni9不锈钢进行了渗硅处理.采用X射线衍射仪(XRD)和附带能量色散谱仪(EDS)附件的扫描电子显微镜(SEM)研究了渗层截面的物相组成、成分,显微形貌及渗硅层的形成机理.结果表明,900 ℃下保温3 h渗层厚度在250 μm以上,渗层物相为富含Cr、Ni合金元素的Fe,Si型金属间化合物,渗层中Si的含量为6.75 wt%,Cr的含量仅为其在基体中含量的50%左右,Ni在基体和渗层中的含量相当,渗层表面致密,硬度在700 HV左右,远高于基体硬度200 HV.

参考文献

[1] Recco AAC;Lopez D;Bevilacqua AF;da Silva F;Tschiptschin AP .Improvement of the slurry erosion resistance of an austenitic stainless steel with combinations of surface treatments: Nitriding and TiN coating[J].Surface & Coatings Technology,2007(4/7):993-997.
[2] Westbrook J H;Fleischer R L.Structural Applications of Intermetallic Compounds[M].New York:John Wiley and Sons,Inc,2000:221.
[3] Jiangang Jia;Qin Ma;Jinjun Lu;Bo Wang .Reciprocating Sliding Friction and Wear Property of Fe{sub}3Si Based Alloys Containing Cu in Water Lubrication[J].Tribology letters,2008(2):113-121.
[4] 蔡珣.表面工程技术工艺方法400种[M].北京:机械工业出版社,2006:246.
[5] Tatemoto, K;Ono, Y;Suzuki, RO .Silicide coating on refractory metals in molten salt[J].The journal of physics and chemistry of solids,2005(2/4):526-529.
[6] 何小凤,李运刚,李智慧.KCl-NaCl-NaF-(SiO2)熔盐体系初晶温度的研究[J].有色金属(冶炼部分),2008(04):12-15.
[7] David R Lide.Handbook of Chemistry and Physics[M].Boca Raton,Florida CRC Press,2007:75-76.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%