以碳酸氢铵为沉淀剂,采用微通道反应与共沉淀法相结合的方法制备出了钇铝石榴石纳米粉体。实验考查了溶液浓度、pH值、Nd3＋掺杂等因素对合成纯相YAG纳米粉体的影响。结果表明增大沉淀剂浓度不利于纯相YAG粉体的制备,当沉淀剂浓度为0.4mol/L,Al 3＋浓度范围为0.1～0.4mol/L的条件下均得到纯相YAG纳米粉体;采用优化的实验条件,体系pH值维持在8左右,以2%（原子分数）的Nd3＋取代YAG中的Y3＋,900℃保温4h得到纯相Nd∶YAG粉体,粉体平均粒径在40nm左右,分布均匀,呈近球形。
YAG nanopowders were preparated by microchannel reaction and co-precipitation method. The experi ment examine the solution concentration, pH, Nd3+ doped and other factors on the synthesis of pure phase YAG powders. The results show that: It is not conducive to the preparation of pure phase YAG powders by in creasing the concentration of precipitant, while precipitant concentration of 0.4mol/L, and Al3+ concentrations ranging from 0.1 to 0.4mol/L, that all obtain pure phase YAG powders; using the optimization experimental condition, the pH value was maintain at about 8, 2at % Nd3+ replace of Y3+ in YAG, after calcined by 900℃ for 4h, pure phase of Nd : YAG powders are obtained. The average particle size of powders was about 40nm, even ly distributed, and show a nearly spherical.
参考文献
| [1] | Yokoyama T.Single crystal for solid-state laser material[J].Bull Ceram Soc Jap,1988(23):461-463. |
| [2] | S.-M. SIM;K. A. KELLER;T.-I. MAH .Phase formation in yttrium aluminum garnet powders synthesized by chemical methods[J].Journal of Materials Science,2000(3):713-717. |
| [3] | Ren Guoguang;Liu Shuying et al.The next generation of solid-state lasers,ceramic laser[J].Laser and Infra- red,2008,38(08):0747-0753. |
| [4] | Sekita M;Haneda H.Optical spectra of un doped and rare earth doped transparent ceramics Y3AIsOI2[J].Journal of Applied Physics,1991(69):3709-3718. |
| [5] | 杨秋红.激光透明陶瓷研究的历史与最新进展[J].硅酸盐学报,2009(03):476-484. |
| [6] | Yagi H;Yanagitani T;Takaichi K.Characteriza dons and laser performances of highly transparent Nd:Y3 AI5O2laser ceramics[J].Optical Materials,2007(29):1258-1262. |
| [7] | Li Shipu.The special ceramic technology[M].Wuhan:Wuhan University of Technologv Press,1990:12. |
| [8] | Ikesue A.;Kamata K.;Yoshida K.;Kinoshita T. .FABRICATION AND OPTICAL PROPERTIES OF HIGH-PERFORMANCE POLYCRYSTALLINE ND-YAG CERAMICS FOR SOLID-STATE LASERS[J].Journal of the American Ceramic Society,1995(4):1033-1040. |
| [9] | Ikesue A.;Yoshida K.;Kamata K. .EFFECTS OF NEODYMIUM CONCENTRATION ON OPTICAL CHARACTERISTICS OF POLYCRYSTALLINE ND-YAG LASER MATERIALS[J].Journal of the American Ceramic Society,1996(7):1921-1926. |
| [10] | Manalert R.;Rahaman MN. .SOL-GEL PROCESSING AND SINTERING OF YTTRIUM ALUMINUM GARNET (YAG) POWDERS[J].Journal of Materials Science,1996(13):3453-3458. |
| [11] | Veith M;Kareiva A;Jilavi M;Zimmer M;Huch V;Mathur S .Low temperature synthesis of nanocrystalline Y sub 3 Al sub 5 O sub 12 (YAG) and Ce-doped Y sub 3 Al sub 5 O sub 12 via different sol-gel methods[J].Journal of Materials Chemistry: An Interdisciplinary Journal dealing with Synthesis, Structures, Properties and Applications of Materials, Particulary Those Associated with Advanced Technology,1999(12):3069-3079. |
| [12] | Li Xia;Liu Hong et al.Production of nanosized YAG powders with spherical morphology and nonaggregation via a solvotherma method[J].Journal of the American Ceramic Society,2004,87(12):22882290. |
| [13] | Wei I.ei;Sun Xudong et al.Fabrication of YAG ultra-fine powder and translucent ceramics by co precipilation method[J].Journal of Functional Materials,2001,35(01):89-91. |
| [14] | Li Hong;Zhang Xudong et al.Solvothermal synthesis and t'ormation mechanism of YAG super-fine powder[J].Journal of Functional Materials,2006,37(01):25-26. |
| [15] | Ji-Guang Li;Takayasu Ikegami .Co-precipitation synthesis and sintering of yttrium aluminum garnet (YAG) powders: the effect of precipitant[J].Journal of the European Ceramic Society,2000(14/15):2395-2405. |
| [16] | Li J G;Ikegami T et al.I.ow-temperature fabrication of transparent yttrium aluminum garnet(YAG)ceram ics without additives[J].Journal of the American Ceramic Society,2000,83(04):961963. |
| [17] | Yang Qing;Wang Jiexin;C-uo Fen et al.Preparaaion of hydroxyapatite nanopowders by using microchannel reaction and hydrothermal crystallization method[J].Ciesc Journal,2010,61(01):235242. |
| [18] | Xing Zheng;Bi Jianqiang;Wang Weili;el al .Effect of pH on preparation of the NHIAIO(OH)HCO3precur sor[J].Journal of Functional Materials,2008,39:668-669. |
| [19] | 王宏志,高濂.共沉淀法制备纳米YAG粉体[J].无机材料学报,2001(04):630-634. |
| [20] | Li Xia .Preparation and characterization of neodymium- doped yttrium aluminum garnet(Nd:YAG)laser ce ramics[D].济南:山东大学,2005. |
| [21] | Naoya Matsushita;Noriyoshi Tsuchiya;Katsuto Nakatsuka;Takakimi Yanagitani .Precipitation and calcination processes for yttrium aluminum garnet precursors synthesized by the urea method[J].Journal of the American Ceramic Society,1999(8):1977-1984. |
| [22] | Cheng Jinping .Preparation and sintering process of Nd:YAG transparent ceramic powders[D].Dalian:1)allan Maritime University,2010. |
| [23] | Li Shuangchun .Preparation examination of laser ceramic powders[D].Xi'an:Xi'an University of Electronic Sei ence and Technology,2007. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%