采用HDI缩二脲封端端羟基丁腈橡胶预聚物,制备大分子橡胶改性活化剂,以氢氧化钠为催化剂,选择不同配比的ABS树脂加入熔融己内酰胺单体中,确定聚合温度为160 ℃～180 ℃,通过阴离子聚合制得ABS/PA6共混物.耐水性和吸水后力学性能分析得知,合金共聚物吸水率比纯PA6明显降低,合金吸水后力学性能有不同程度的降低,但吸水后力学损失量比纯PA6低很多.电镜测试表明原位反应增容因PA6与ABS两相界面张力降低,使ABS分散颗粒变小并更均匀地分散于PA6中.
参考文献
| [1] | Aoki Y;Watanabe M .[P].US 4987185,1991. |
| [2] | Majumdar B;Keskkula H;Paul D R .[J].Polymer,1994,35:5453-5467. |
| [3] | Majumdar B;Keskkula H;Paul D R .[J].Polymer,1994,35:5468-5477. |
| [4] | 谢静薇,刘强,谢文炳,王巍.PA-6/ABS共混体系中加入SMA的反应型增容作用[J].高分子材料科学与工程,1999(05):87-90. |
| [5] | Kudva R A;Keskkula H;Paul D R .[J].Polymer,2000,41(01):225-237. |
| [6] | Kitayama N.;Paul DR.;Keskkula H. .Reactive compatibilization of nylon 6/styrene-acrylonitrile copolymer blends. Part 2. Dispersed phase particle size[J].Polymer: The International Journal for the Science and Technology of Polymers,2000(22):8053-8060. |
| [7] | Kudva R A;Keskkula H;Paul D R .[J].Polymer,2000,41(01):239-258. |
| [8] | Padwa A R;Lavengood R E .[J].Polymeric Preprints,1992,33(02):600-601. |
| [9] | 王璐,郭宝华,谢续明.ABS的MAH/St多单体熔融接枝及其对PA6/ABS共混体系相形态和力学性能的影响[J].高分子学报,2005(02):213-218. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%