采用三因素四水平正交实验与单因素实验相结合,通过力学性能测试及SEM和光学显微镜微观形貌观察研究了复合材料铺放过程中压紧力、预浸带加热温度及芯模温度对复合材料力学性能的影响。实验结果表明：压紧力与加热温度对层间剪切强度（ILSS）影响很大,而芯模温度影响较小;当压紧力为600N、预浸带加热温度为30℃、芯模温度为18℃时,复合材料综合力学性能达到最佳。微观形貌观察结果表明：随着压紧力和预浸带加热温度升高,纤维与树脂接触充分,树脂与纤维分布均匀性较好,层间富树脂区的厚度较小,ILSS逐渐增加;但当预浸温度上升到40℃以后,压紧力作用导致树脂与纤维的分布均匀性变差,层间富树脂区的厚度较大,从而导致ILSS下降。
The orthogonal experiment of three factors-four levels and a single factor experiment were conducted to evaluate the effect of compaction force,heating temperature of prepreg,and tool temperature on the mechanical properties of the laminar composite fabricated by fiber placement.The testing results of the mechanical properties and the microstructure images obtained through SEM and light microscope show that the effect of compaction force and heating temperature on interlaminar shear-strength（ILSS） is significant,while the effect of the tool temperature on ILSS is not obvious.The comprehensive mechanical properties of laminar composite are the best at 600 N level of the compaction force,30 ℃ of the heating temperature,and 18 ℃ of the tool temperature.The microstructure results show that the distribution of resin in the cured composite becomes more and more uniform,and the thickness of interlaminar resin-rich area decreases with the increase of compaction force and heating temperature,and accordingly the strong ILSS.When the heating temperature is over 40 ℃,the distribution of resin in the cured composite material becomes non-uniform because of the action of compaction force,the thickness of interlaminar resin-rich area increases gradually,which results in the decrease of ILSS.
参考文献
| [1] | Harris Charles E, Starnes James H, Shuart Mark J, Jr. Design and manufacturing of aerospace composite structures, state-of-the-art assessment [J]. Journal of Aircraft, 2002, 39 (4) : 545-560. |
| [2] | Tadich Josef Kryger, Wedel- Heinen Jakob, Petersen Peter. New guidance for the development of wind turbine blades [C]// Copenhagen Offshore Wind 2005. Copenhagen: European Wind Energy Association, 2005 |
| [3] | 李勇,肖军.复合材料纾维铺放技术及其应用[J].纤维复合材料,2002(3):39-41. |
| [4] | 王志辉,吕佳.纤维铺放头机构的研究[J].机械工程师,2007(12):93-94. |
| [5] | De Vlieg Russell, Jeffries Kyle, Vogeli Peter. High - speed fiber placement on large complex structures, 2007 - 01 - 3843 [R]. USA: SAE International, 2007. |
| [6] | Khan Muhammad Amir, Mitschang Peter, Schledjewski Ralf. Identification of some optimal parameters to achieve higher laminate quality through tape placement process [M]. Hoboken, NJ: Wiley Subscription Services, Inc, 2010: 98-111 |
| [7] | Shih Po-Jen. On - line consolidation of thermoplastic composites [D]. Virginia: Virginia Polytechnic Institute & State University, 1997. |
| [8] | Compston P, Schiemer J, Cvetanovska A. Mechanical properties and styrene emission levels of a UV- cured glass- fihre/vinylester composite[J]. Composite Structures, 2008, 86(1-3): 22-26. |
| [9] | Lee Munki. Heat transfer and consolidation modeling of composite fiber tow in fiber placement I-D']. Virginia: Virginia Polytechnic Institute State University, 2004 |
| [10] | 沈真,杨胜春,柴亚南.国外复合材料试验标准汇编[M].西安:中国飞机强度研究所,2007. |
| [11] | 李岚,袁莉,梁国正.工艺参数对聚脲甲醛包覆环氧树脂微胶囊物性的影响[J].复合材料学报,2006,23(5):51-57. |
| [12] | 郭慧.碳纤维表面能、表面粗糙度及化学组成的表征[D].哈尔滨:哈尔滨工业大学,2010. |
| [13] | 朱黎黎,张佐光,李敏,等.工艺温度下树脂与纤维的接触角及其粘附作用研究[J].复合材料学报,2010,27(5):41-46. |
| [14] | 李卫东,曹海琳,刘毅佳,等.胶含量对CF/BF复合材料性能的影响[J].宇航材料工艺,2010,27(1):49-52. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%