采用背散射电子衍射分析技术(EBSD)和慢应变速率拉伸实验方法研究不同轧制道次的Inconel 690合金微观组织和应力腐蚀开裂(scc)行为.结果表明,三道次轧制的690合金样品的晶粒更大,低重合点阵晶界所占比例更高,织构程度更弱.三道次轧制的690合金在高温高压纯水中的慢应变速率拉伸试验表现出更好的耐应力腐蚀性能.三道次轧制的690合金可以形成更加均匀的组织,提高低重合点阵晶界所占比例,增加其抗应力腐蚀能力.

参考文献

[1] Lee W S,Liu C Y,Sun T N .Deformation behavior of lnconel 690 super alloy evaluated by impact test[J].J Mater Process Technol,2004,153:219-225.,2004.
[2] Lin Y S,Kim J S,Kim H P,et al .The effect of grain boundary misoritation on the intergranular M23C6 carbide precipitation in thermally treated alloy 690[J].Journal of Nuclear Materials,2004,335
[3] Xia S,Zhou B X,Chen W J .Grain cluster microstructure and grain boundary character distribution in alloy 690[J].Metallurgival and Materials Transactions A,2009,40(12):3016-3030.,2009.
[4] Randle V .Application of electron backscatter diffraction to grain boundary characterization[J].International Materials Review,2004,49(1):1-11.,2004.
[5] Zhang Z M,Wang J Q,Han E H,et al .Trans-twins stress corrosion cracking behaviors of Alloy 690TT in lead-containing caustic solution at 330 ℃[J].Nuclear Engineering and Design,2011,241
[6] Peng Q J,Hou J,Yonezawa T,et al .Environmentally assisted crack growth in one-dimensionally cold worked alloy 690TT in primary water[J].Corrosion Science,2012,57
[7] Peng B,Lu B T,Luo J L,et al .Investigation of passive films on nickel Alloy 690 in lead-containing environments[J].Journal of Nuclear Materials,2008,378(3):333-340.,2008.
[8] Dutta R S,Tewari R,De P K .Effects of heat-treatment on the extent of chromium depletion and caustic corrosion resistance of alloy 690 original research[J].Corrosion Science,2007,49(2):303-318.,2007.
[9] Dutra R S,Tewari R,De P K .Effects of heat-treatment on the extent of chromium depletion and caustic corrosion resistance of alloy 690[J].Corrosion Science,2007,49(2):303-318.,2007.
[10] 李成涛,刘飞华,李岩,程学群,董超芳,李晓刚.固溶温度对690合金在NaOH溶液中的电化学性能影响[J].材料热处理学报,2011(09):48-52.
[11] 李成涛,宋利君,任爱,刘飞华,李岩,程学群,李晓刚.Inconel 690合金在含Pb碱溶液中的应力腐蚀行为[J].材料热处理学报,2013(10):38-42.
[12] Li H,Xia S,Zhou B,et al .C-Cr segregation at grain boundary before the carbide nucleation in alloy 690[J].Materials Characterization,2012,27(3):68-74.,2012.
[13] 杨亮,董建新,何智勇,张麦仓.基于组织均匀性的690合金管冷轧及退火工艺优化[J].北京科技大学学报,2012(04):410-416.
[14] Shimada M,Kokawa H,Wang Z J,et al .Optimization of grain boundary character distribution for intergranular corrosion resistant of 304 stainless steel by twin-induced grain boundary engineering[J].Acta Materialia,2002,50(9):2331-2341.,2002.
[15] Alexandreanu B,Was G S .The role of stress in the efficacy of coincident site lattice boundaries in improving creep and stress corrosion cracking[J].Scripta Materialia,2006,54(6):1047-1052.,2006.
[16] Ravi Kumar B,Singh R,Mahato B,et al .Effect of texture on corrosion behavior of AISI 304L stainless steel[J].Materials Characterization,2005,54
[17] 李成涛,宋利君,任爱,刘飞华,李岩,李晓刚,程学群.690合金在核电一回路水环境的应力腐蚀行为[J].哈尔滨工程大学学报,2013(11):1465-1470.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%