本文研究了热等静压处理对IN792材料组织和持久性能的影响.结果表明,IN792材料经1180℃/150 MPa热等静压处理后显微疏松完全闭合.与直接热处理样品相比,热等静压处理后样品中的共晶含量减少；枝晶干处y’相的体积分数和尺寸增大,分别由34％,0.4 μm增大至42％,0.56μ.760℃/655 MPa和870℃/365 MPa条件下持久性能测试表明,热等静压处理均显著提高了材料的持久寿命.
参考文献
| [1] | Jian Zhang .Effect of Ti and Ta on hot cracking susceptibility of directionally solidified Ni-based superalloy IN792[J].Scripta materialia,2003(6):677-681. |
| [2] | 郭建亭.高温合金材料学[M].北京:科学出版社,2008 |
| [3] | Kim M T;Chaug S Y;Won J B .Effect of HIP process on the micro-structural evolution of anickel-based superalloy[J].Materials Science and Engineering,2006,441(1-2):126-134. |
| [4] | Apparao G;Kumar M;Srinivas M et al.Effect of solution treatment temperature on the microstructure and tensile properties of P/M (HIP)processed superalloy Inconel 718[J].Journal of Materials Science and Technology,2003,19:605-616. |
| [5] | J. ZHANG;R. F. SINGER .Effect of Zr and B on Castability of Ni-Based Superalloy IN792[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2004(4):1337-1342. |
| [6] | Petrenec M;Obrtlík K;Polák J et al.Fatigue behaviour of a cast nickle-based superalloy Inconel 7925-5A at 700 ℃ utrujanje lite niklje superzlitine Inconel 7925-5A PRI 700 ℃[J].Materialiin tehnologije,2006,40(05):667-672. |
| [7] | Jinxia Yang;Qi Zheng;Hongyu Zhang;Xiaofeng Sun;Hengrong Guan;Zhuangqi Hu .Effects of heat treatments on the microstructure of IN792 alloy[J].Materials Science & Engineering. A, Structural Materials: Properties, Misrostructure and Processing,2010(4/5):1016-1021. |
| [8] | 蔡玉林;郑运荣.高温合金的金相研究[M].北京:国防工业出版社,1986 |
| [9] | 陈国良.高温合金学[M].北京:冶金工业出版社,1988 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%