用晶体取向分布函数研究了含0.13％Cu的低碳镇静钢冷轧薄板再结晶退火过程织构的变化。结果表明,冷轧织构主要为平行于板面法线的<111>纤维织构组分和{001} <110>组分;此两组分的漫散构成平行于轧向的<110>部分纤维织构。在再结晶过程中<111>纤维织构增强,{001} <110>组分减弱,因而<110>部分纤维织构也逐渐收缩,表明它不是一个独立的织构组分。
The change of texture during recrystallization annealing in low carbon Alkilled steel sheet containing 0.13% Cu has been studied by function of crystal orientation distribution. It is shown that the cold-rolled texture is composed of one component of the <111> fibre texture with fibre axis parallel to the plane normal and another component of {001} <110>. The <110> partial fibre texture with fibre axis parallel to the rolling direction is formed by the diffusion of the two components. During the recrystallization, <111> fibre texture becomes prevailing and {001} <110> component diminishes while the <110> partial fibre texture contracts gradually, therefore, the <110> partial fibre texture is not an independent one.
参考文献
| [1] | |
| [2] | |
| [3] | |
| [4] | |
| [5] | |
| [6] | |
| [7] | |
| [8] | |
| [9] | |
| [10] | |
| [11] | |
| [12] | |
| [13] | |
| [14] | |
| [15] | |
| [16] |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%