800 MPa grade new ultra-low carbon bainitic (NULCB) steel is the recently developed new generation steel.The microstructure in the coarse-grained heat-affected zone (CGHAZ) of NULCB steel under laser welding conditions was investigated by thermal simulation. The influence of the cooling time from 800℃ to 500℃,t8/5 (0.3~30 s), on the microstructure of the CGHAZ was discussed. The experimental results indicate that the microstructure of the CGHAZ is only the granular bainite which consists of bainitic ferrite (BF) lath and M-A constituent while t8/5 is 0.3~30 s. The M-A constituent consists of twinned martensite and residual austenite, and the change of the volume fraction of the residual austenite in the M-A constituent is very small when t8/5 is between 0.3 and 30 s. The morphology of the M-A constituent obviously changes with the variation of t8/5. As t8/5 increases, the average width, gross and shape parameter of the M-A constituent increase, while the line density of the M-A constituent decreases.

参考文献

[1] X.M. WANG;X.L. HE;S.W. YANG .Refining of Intermediate Transformation Microstructure by Relaxation Processing[J].ISIJ International,2002(12):1553-1559.
[2] 王学敏,尚成嘉,杨善武,贺信莱.组织细化的控制相变技术机理研究[J].金属学报,2002(06):661-666.
[3] Shanwu Yang,Xuemin Wang,Chengjia Shang,Xinlai He,Yi Yuan.Relaxation of Deformed Austenite and Refinement of Bainite
[4] Chengjia Shang,Xuemin Wang,Shanwu Yang,Xinlai He.Refinement of packet size in low carbon bainitic steel by special thermo-mechanical control process[J].北京科技大学学报(英文版),2004(03):221-224.
[5] Xudong ZHANG,Wuzhu CHEN,Cheng Wang,Lin ZHAO,Yun Peng,Zhiling TIAN.Microstructures and Toughness of Weld Metal of Ultrafine Grained Ferritic Steel by Laser Welding[J].材料科学技术学报(英文版),2004(06):755-759.
[6] Y Peng;Z L Tian;C Wang;W Z Chen G Bao,L Zhao .[J].Steel Research International,2002,73(11):508.
[7] Xudong ZHANG,Wuzhu CHEN,Gang Bao,Lin ZHAO.Improvement of Weld Quality Using a Weaving Beam in Laser Welding[J].材料科学技术学报(英文版),2004(05):633-636.
[8] J H Chen;Y Kikuta;T Araki;M Yoneda,Y Matsuda .[J].Acta Metallurgy,1984,32(10):1779.
[9] Chunxiao HOU .[D].北京:清华大学,1985.
[10] Hongsheng FANG;Haijin DENG .[J].Mater Mechan Eng,1981,5(01):5.
[11] F Matsuda;K Ikeuchi;J Liao .[J].Transactions of JWRI(Joining and Welding Research Institute of Osaka University),1993,22(02):271.
[12] M Nakanishi;Y Komizo;Y Fukada .[J].Quarterly Journal of Japan Welding Society,1986,4(02):447.
[13] Y Komizo;Y Fukada .[J].Quarterly Journal of Japan Welding Society,1988,6(01):41.
[14] D W Tian;L P Karjalainen;B N Qian;X F Chen .[J].JSME International Journal,1997,40(02):179.
[15] K Y Lam;W Cao;T Zhuang .[J].Engineering Fracture Mechanics,1993,44(05):753.
[16] Hongyang JING;Lixing HUO;Yufeng ZHANG .[J].Trans China Weld Inst,1997,18(01):37.
[17] F Matsuda;Y Fukada;H Okada;C Shiga K Ikeuchi Y Horii T Shiwaku,S Suzuki .[J].Welding in the World,1996,37(03):134.
[18] F Matusda;K Ikeuchi;H Okada;I Hrivnak,H Park .[J].Transactions of JWRI(Joining and Welding Research Institute of Osaka University),1994,23(02):231.
[19] F Kawabata;N Itakura;H Y Jing;K Amano F Minami,M Toyoda .[J].JSNA Journal,1993,173:349.
[20] Guiquan YIN;Jiasheng GAO;Yongchang HONG;Rui CHEN .[J].Trans China Weld Inst,2001,22(02):71.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%