采用高温固相法,在掺硫和不掺硫两种情形下制备了Sr3Al2O6:Eu, Dy红色长余辉发光材料. 利用XRD、荧光分光光度计和亮度计,分别研究了材料的晶体结构、激发光谱、发射光谱和衰减曲线. 结果表明:硫的掺入没有引起Sr3Al2O6激发峰的变化,但对材料的组成,初始亮度和余辉特性有明显影响. 在同一烧结温度下,未掺硫的样品主晶相为Sr3Al2O6,并有少量杂相Sr4Al2O7,初始亮度为148 mcd·m-2,余辉时间为330 s; 掺硫的样品主晶相为Sr3Al2O6,含有少量杂项SrS,初始亮度为505 mcd·m-2,余辉时间为18 min.
参考文献
| [1] | Smets B;Rutten J;Hoeks G .2SrO·3Al2O3:Eu2+ and 1.29(Ba,Ca)O·6Al2O3:Eu2+ two new blue-emitting phosphors[J].Journal of the Electrochemical Society,1989,136(07):2119. |
| [2] | 唐明道,李长宽,高志武,许少鸿,蒋雪茵,蔡锟.SrAl2O4：Eu2+的长余辉发光特性的研究[J].发光学报,1995(01):51-56. |
| [3] | Jorma Holsa;Hogne Jungner;Mika Lastusaari .Persistent luminescence of Eu~(2+) doped alkaline earth aluminates, MAl_2O_4:Eu~(2+)[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2001(0):326-330. |
| [4] | Wang Minquan;Dong Wang;Lü Guanglie .Research on fluorescence spectra and structure of single-phase 4SrO@7Al2O3:Eu2+ phosphor prepared by solid-state reaction method[J].Materials Science and Engineering,1998,B57:18. |
| [5] | Peng Tianyou;Liu Huajun;Yang Huanping;Yan Chunhua .Synthesis of SrAl2O4:Eu,Dy phosphor nanometer powders by sol-gel processes and its optical properties[J].Materials Chemistry and Physics,2004,85:68. |
| [6] | Capron M;Douy A;Am J .Strontium dialminate SrAl4O7 synthesis and stability[J].Ceramic Society,2002,85:3036. |
| [7] | 刘阁,梁家和,邓兆祥,李亚栋.新型红色荧光粉Sr3Al2O6的合成和发光性能研究[J].无机化学学报,2002(11):1135-1137. |
| [8] | 苏锵,梁宏斌,陶冶,王淑彬.稀土离子的高能光谱[J].中国稀土学报,2001(06):481-486. |
| [9] | Lu Liping;Zhang Xiaoyan;Bai Zhaohui et al.Synthesis and characterization of IR up-conversion material SrS:Eu,Sm[J].Journal of Rare Earths,2005,23(01):44. |
| [10] | 张迈生,王立格,杨燕生.SrS：Ce3+,K+荧光体的微波辐射合成法及对发光特性的影响[J].稀土,1999(03):31-33. |
| [11] | 蒙延双,王达健,李岚,施哲.锶铝比对稀土掺杂铝酸锶物相及发光性能的影响[J].中国稀土学报,2005(03):277-280. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%