分别以机械混合法和浸渍法制备了SO2-4/SiO2-TiO2固体酸催化剂,以乙醇和乙酸的酯化反应为模型反应考察了不同SiO2含量及不同温度焙烧的催化剂的活性. 结果表明,机械混合法制备的400 ℃焙烧的SO2-4/40%SiO2-TiO2催化剂活性最高,部分回流时,乙酸几乎全部转化,全回流反应100 min时,其乙酸转化率达到84%. X射线衍射分析表明, SiO2抑制了硫酸氧钛的形成; 催化剂的活性组分包括一定量的四方晶锐钛矿型TiO2、正交晶硫酸氧钛、少量立方晶金属钛和高比表面积的SiO2. 红外光谱分析表明,添加SiO2后催化剂形成 Ti - O - Si 键,进而使SO2-4与样品表面产生强相互作用; 结合的SO2-4主要以无机螯合状双配位和有机硫酸酯两种结构形式存在. 热重-示差扫描量热分析表明, SiO2的添加使SO2-4不易脱除,同时使锐钛矿TiO2向金红石相的转变温度降低.
参考文献
| [1] | Luo Z Y;Wang S R;LiaoY F;Zhou J S, Gu Y L, Cen K F .[J].Biomass and Bioenergy,2004,26(05):455. |
| [2] | Sipila K.;Kuoppala E.;Fagernas L.;Oasmaa A. .Characterization of biomass-based flash pyrolysis oils[J].Biomass & Bioenergy,1998(2):103-113. |
| [3] | Ramu S;Lingaiah N;Devi BLAP;Prasad RBN;Suryanarayana I;Prasad PSS .Esterification of palmitic acid with methanol over tungsten oxide supported on zirconia solid acid catalysts: effect of method of preparation of the catalyst on its structural stability and reactivity[J].Applied Catalysis, A. General: An International Journal Devoted to Catalytic Science and Its Applications,2004(1/2):163-168. |
| [4] | Moghaddam M K;Gholami M R .[J].Materials Letters,2006,60(06):715. |
| [5] | 王绍艳,张志强,吕玉珍,侯鑫.纳米固体超强酸SO42-/Fe2O3的制备及其催化合成乙酸乙酯[J].无机化学学报,2002(03):279-283. |
| [6] | 常铮,郭灿雄,段雪,张密林.磁性超细固体酸催化剂SO2-4-ZrO2/Fe3O4的组装及表征[J].催化学报,2003(01):47-51. |
| [7] | 周以力.乙酸乙酯制备实验中化学平衡的研究[J].嘉兴学院学报,2003(03):44-46. |
| [8] | 高鹏,崔波.低温沉淀法制备固体超强酸及其对酯化反应的催化作用[J].石油化工,2004(01):5-8. |
| [9] | 曹剑瑜,卢文庆,焦程敏,王鹏飞.纳米TiO2的合成、表征及紫外吸收性能[J].南京师大学报(自然科学版),2004(01):51-54. |
| [10] | Zhao Y X;Xu L P;Wang Y Z;Gao C G, Liu D S .[J].Catalysis Today,2004,93-95:583. |
| [11] | Jung S M;Dupont O;Grange P .[J].Applied Catalysis A:General,2001,208(1-2):393. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%