通过碳热还原法制备(Ti,W,Mo)C预合金化固溶体粉末,采用粉末冶金法制备(Ti,W,Mo)C-Ni金属陶瓷,研究了烧结温度对金属陶瓷致密性、组织与性能的影响.结果表明:在1 410～1 470℃范围内,随烧结温度提高,金属陶瓷的硬度提高,致密性先提高后略下降;在1 450℃时制备的金属陶瓷晶粒细小、组织均匀致密,呈现最佳综合力学性能,横向断裂强度为1 751 MPa,硬度为91.3 HRA.
参考文献
| [1] | P.Lindahl;P.Gustafson .Microstructure of model cermets with high Mo or W content[J].International Journal of Refractory Metals & Hard Materials,1999(8):411-421. |
| [2] | 章晓波,刘宁,袁红梅,荣春兰.化学成分对TiC-Ni系金属陶瓷显微组织的影响[J].硬质合金,2008(01):6-11. |
| [3] | Sun-Yong Ahn;Seong-Won Kim;Shinhoo Kang .Microstructure of Ti(CN)-WC-NbC-Ni Cermets[J].Journal of the American Ceramic Society,2001(4):843-849. |
| [4] | Youngjae Kang;Shinhoo Kang .WC-reinforced (Ti,W)(CN)[J].Journal of the European Ceramic Society,2010(3):793-798. |
| [5] | Xiao Chen;Weihao Xiong;Jun Qu .Microstructure and mechanical properties of (Ti,W,Ta)C-xMo-Ni cermets[J].International Journal of Refractory Metals & Hard Materials,2012(Mar.):56-61. |
| [6] | Yongzhong Jin;Ying Liu;Yankun Wang .Synthesis of (Ti, W, Mo, V)(C, N) nanocomposite powder from novel precursors[J].International Journal of Refractory Metals & Hard Materials,2010(4):541-543. |
| [7] | 刘文俊,郑勇,游敏.烧结温度对细晶粒Ti（C,N）基陶瓷组织和性能的影响[J].三峡大学学报(自然科学版),2003(02):114-117. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%