采用扫描电镜(SEM)、X光电子能谱分析仪(XPS)等分析手段,研究了NiTi合金表面绝缘膜的结构及成分,从而探讨非阀金属NiTi合金表面微弧氧化陶瓷膜层的形成机制.结果表明,NiTi合金微弧氧化过程中的电流密度-时间曲线与纯钛形状基本一致,也可分为3个阶段,但其最大的电流密度为后者的13倍;NiTi合金表面的绝缘膜主要是通过电化学沉积形成的Al2O3及少量的TiO2、Ni2O3和磷酸盐薄膜,这一绝缘膜就相当于阀金属的阳极氧化膜,为NiTi合金进行微弧氧化处理提供了前提条件;NiTi合金表面的陶瓷膜层主要来源于电解液中的铝酸根离子和少量的基体Ni和Ti(包括固态的和溶解于电解液中离子态的),经反复的放电、熔融、喷射、冷却、凝固,发生一系列的电化学、等离子体化学和热化学反应最终形成表面粗糙多孔陶瓷膜层.
参考文献
| [1] | Yerokhin A L;Nie X;Layland A et al.[J].Surface and Coatings Technology,1999,122(2-3):73. |
| [2] | 李兆峰,廖志谦,匡蒙生,蒋鹏,张建欣.Ti-6Al-2Zr-1Mo-3Nb合金微弧氧化陶瓷膜的结构与性能[J].稀有金属材料与工程,2011(01):40-44. |
| [3] | Sul YT .The significance of the surface properties of oxidized titanium to the bone response: special emphasis on potential biochemical bonding of oxidized titanium implant.[J].Biomaterials,2003(22):3893-3907. |
| [4] | Wang Yaming;Lei Tingquan;Jiang Bailing et al.[J].Applied Surface Science,2004,233:258. |
| [5] | Güntherschlze A;Betz H .[J].Zeitschrift für Physik,1934,78(91):70. |
| [6] | 薛文斌,王超,马辉,谢孟峡,陈如意,邓志威.TA2纯钛表面微弧氧化膜的成分和相结构分析[J].稀有金属材料与工程,2002(05):345-348. |
| [7] | Cui S H;Han J M;Du Y P et al.[J].Surface and Coatings Technology,2007,201(9-11):5306. |
| [8] | Wu K;Wang Y Q;Zheng M Y .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2007,447:227. |
| [9] | Liu L;Liu Z;Chan K C et al.[J].Scripta Materialia,2008,58:231. |
| [10] | Wang Y L;Jiang Z H .[J].Applied Surface Science,2009,255(12):6240. |
| [11] | Wang, YL;Jiang, ZH;Yao, ZP .Preparation and properties of ceramic coating on Q235 carbon steel by plasma electrolytic oxidation[J].Current applied physics: the official journal of the Korean Physical Society,2009(5):1067-1071. |
| [12] | Liang J;Hu L T;Hao J C .[J].Electrochimica Acta,2007,52(14):4836. |
| [13] | Sun X T;Jiang Z H;Xin S G et al.[J].Thin Solid Films,2005,471(1-2):194. |
| [14] | Wu Z D;Yao Z P;Jiang Z H .[J].Rare Metals,2008,27(01):55. |
| [15] | Shabalovskaya S A .[J].Biomedical Materials & Engineering,1996,6:267. |
| [16] | Mckay GC.;Macdonald C.;Grant MH.;Macnair R. .INTERACTIONS OF ORTHOPAEDIC METALS WITH AN IMMORTALIZED RAT OSTEOBLAST CELL LINE[J].Biomaterials,1996(13):1339-1344. |
| [17] | Xu J L;Liu F;Wang F P et al.[J].Applied Surface Science,2008,254:6642. |
| [18] | Xu J L;L iu F;Wang F P et al.[J].Materials Letters,2008,62:4112. |
| [19] | Liu, F.;Xu, J.;Wang, F.;Zhao, L.;Shimizu, T. .Biomimetic deposition of apatite coatings on micro-arc oxidation treated biomedical NiTi alloy[J].Surface & Coatings Technology,2010(20):3294-3299. |
| [20] | Firstov G S;Vitchev R G;Kumar H et al.[J].Biomaterials,2002,23:4863. |
| [21] | Oji M O;Wood J V .[J].Journal of Materials Science:Materials in Medicine,1999,10:869. |
| [22] | Krysmann W;Kurze P;Dittrich K H et al.[J].Crystal Research and Technology,1984,19(07):973. |
| [23] | Van T B;Brown S D;Wirlz G P .[J].American Ceramic Society Bulletin,1977,56(06):563. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%