以聚环氧乙烷/高氯酸锂络合物(PEO/LiCIO4)为基体,前驱体正硅酸乙酯(TEOS)在基体中水解缩合原位生成纳米SiO2,制备了PEO/LiCIO4/SiO2复合聚电解质膜,采用AFM、DSC和交流阻抗等方法研究了聚电解质膜的表面形貌、热性能和离子电导率.结果表明,原位生成的纳米SiO2粒子,均匀分散于PEO基体中,复合纳米SiO2后聚电解质膜的玻璃化转变温度和结晶度均降低,聚电解质膜的离子导电行为满足Arrhenius方程,并在10%SiO2含量时体系的电导率出现最大值2.6×10-5 S/cm(30℃).以此膜为电解质组装的全固态聚合物锂电池放电电压平稳,初始放电比容量为115mAH·g-1,40次循环后放电容量保持在92 mAh·g-1.
参考文献
| [1] | Wang M K;Zhao F;Dong S J .[J].Journal of Physical Chemistry,2004,108:1365. |
| [2] | 伊廷峰;胡信国 .[J].稀有金属材料与工程,2006,35(02):9. |
| [3] | Kim YT.;Smotkin ES. .The effect of plasticizers on transport and electrochemical properties of PEO-based electrolytes for lithium rechargeable batteries[J].Solid state ionics,2002(1/2):29-37. |
| [4] | Ahn J H;Wang G X;Liu H K et al.[J].Journal of Power Sources,2003,119-121:422. |
| [5] | Croce F;Appetecchi G B;Persi L et al.[J].Nature,1998,394:456. |
| [6] | Capiglia C;Mustarelli P et al.[J].Solid State Ionics,1999,118:73. |
| [7] | 王诚,徐鹏,毛宗强,王利生,葛凯勇,徐景明.纳米TiO2复合膜的制备及在燃料电池中的应用[J].稀有金属材料与工程,2006(09):1432-1436. |
| [8] | 毋伟,贾梦秋,陈建峰,邵磊,初广文.硅烷偶联剂对溶胶凝胶法纳米二氧化硅复合材料制备及应用的影响[J].复合材料学报,2004(02):70-75. |
| [9] | Liu Y;Lee J Y;Hong L .[J].Journal of Power Sources,2004,129:303. |
| [10] | Xi J Y;Miao S J;Tang X Z .[J].Mocromolecules,2004,37:8592. |
| [11] | Kim J W;Ji K S;Lee J P et al.[J].Journal of Power Sources,2003,119:415. |
| [12] | Wieczorek W;Zalewska A;Siekierski M et al.[J].Solid State Ionics,1996,86:357. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%