铁基材料由于其可降解性和无毒性,在血管支架材料领域具有潜在的应用前景.采用40kV的氮离子注入工业纯铁,注入剂量为1×1017～7×1017ions/cm2, X射线衍射表征了材料表面的物相结构,采用原子力显微镜研究了离子注入剂量对材料表面形貌的影响,并用Ra、RMS和Rz定量研究了离子注入后的表面粗糙度.结果表明,氮离子注入对纯铁表面形貌产生了一定的影响,随着注入离子剂量的增加,材料表面的粗糙度也随之增加.
参考文献
| [1] | Weber T.;Saris FW.;Koniger A.;Rauschenbach B.;Wolf GK. Krauss S.;Dewit L. .HARDNESS AND CORROSION RESISTANCE OF SINGLE-PHASE NITRIDE AND CARBIDE ON IRON[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1995(2):205-210. |
| [2] | Li MY.;Krishnadev M.;Knystautas EJ. .Enhanced microhardness of four modern steels following nitrogen ion implantation[J].Surface & Coatings Technology,2001(2/3):220-228. |
| [3] | Oztürk O;Türkan U;Eroglu A E .[J].Surface and Coatings Technology,2006,200:5687-5697. |
| [4] | Huang N;Yang P;Leng YX;Wang J;Sun H;Chen JY;Wan GJ .Surface modification of biomaterials by plasma immersion ion implantation[J].Surface & Coatings Technology,2004(1/2):218-226. |
| [5] | 朱生发,徐莉,黄楠,石志峰,刘恒全,张勇.氮离子注入纯铁在人工模拟体液中的腐蚀性能研究[J].功能材料,2007(09):1540-1542. |
| [6] | Jagielski J;Piatkowska A;Aubert P;Thome L;Turos A;Kader AA .Ion implantation for surface modification of biomaterials[J].Surface & Coatings Technology,2006(22/23):6355-6361. |
| [7] | Hecker J;Scandrett L .[J].Journal Biomedical Material Research,1985,19(04):381-395. |
| [8] | 伍媛婷,王秀峰,程冰.原子力显微镜在材料研究中的应用[J].稀有金属快报,2005(4):33-37. |
| [9] | 游俊富,王虎,赵海山.扫描探针显微镜在粗糙度、纳米尺寸、表面形貌观测方面的应用[J].现代科学仪器,2003(02):9-12. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%