用共浸渍法制得了Pt-Rh-Pd/CeO2-La2O3/Al2O3催化剂，采用X射线衍射(XRD)对催化剂进行表征，使用配气测试系统对催化剂的活性进行评价。正交试验结果表明，对CO的氧化，恒择最佳催化剂的配比为Pt-Rh-Pd 0.1%，CeO25%，La2O34%，对NO的还原，其最佳配比为Pt-Rh-Pd 0.1%， CeO24%，La2O34%。稀土氧化物(La2O3、CeO2)作为助剂，能改善Pt-Rh-Pd/CeO2-La2O3/Al2O3催化剂的催化性能，但不能起主要作用。
The Pt-Rh-Pd/CeO2-La2O3/Al2O3 catalysts were prepared with method of co-impregnation, and characterized by X-ray diffraction (XRD). Its catalytic activities were evaluated bygas mixing test system. The results of orthogonal experimentsshowed that the best catalyst formula is Pt-Rh-Pd 0.1%, CeO25%, La2O34% to the oxidation of carbon monoxide, while to the reduction of NO, the best catalyst formula is Pt-Rh-Pd 0.1%, CeO24%, La2O34%. Rare earth oxides (La2O3, CeO2) as co-catalyst, only can improve catalytic ability of Pt-Rh-Pd/CeO2-La2O3/Al2O3, but do not play critical roles.
参考文献
| [1] | 旷成秀,刘康强,李风仪.铑含量对Pt-Rh-Pd/Al2O3催化剂的氧化还原性能的影响[J].江西化工,2005(03):86-88. |
| [2] | 刘振林,屠兢,伏义路.NO在氧化铝负载的Pd催化剂上吸附的TPD-MS研究[J].催化学报,2000(03):279-282. |
| [3] | 唐晓兰,张保才,李勇,辛勤,申文杰.用于CO选择氧化反应的新型Pt-Fe/Al2O3催化剂[J].催化学报,2005(01):1-3. |
| [4] | 罗来涛,郭建军,杨美华,陈昭平,李松军,李凤仪.铈对混合型贵金属尾气净化催化剂性能的影响[J].南昌大学学报(理科版),2003(01):45-48. |
| [5] | 郭建军,杨美华,陈昭平,李松军,罗来涛.镧对混合型贵金属尾气净化催化剂性能的影响[J].江西科学,2002(01):27-30. |
| [6] | 李宁,王爱琴,郑明远,王晓东,张涛.Pd/硫酸化氧化铝--一种新型甲烷选择还原NO催化剂[J].催化学报,2003(11):809-810. |
| [7] | Mengjin LI,Xiaofeng SUN,Hengrong GUAN,Xiaoxia JIANG,Zhuangqi HU.Oxidation Behavior of Pd-Modified Aluminide Coating at High Temperature[J].材料科学技术学报(英文版),2003(03):213-217. |
| [8] | 旷成秀,刘康强,李凤仪.Pt-Rh-Pd/Al2O3三元催化剂的制备及其表征[J].贵金属,2013(01):17-20,24. |
| [9] | 赵选民.实验设计方法[M].北京:科学出版社,2006:236-243. |
| [10] | 黄仲涛;耿建铭.工业催化[M].北京:化学工业出版社,2006:22-24. |
| [11] | 严洪杰;杨骏英;周德幢 等.CeO2对Ni/γ-Al2O3,Pt/γ-Al2O3中Ni、Pt分散度的影响[J].天然气化工,1992,17(05):26-30. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%