采用传统固相法对(1-x)K0.44Na0.52Li0.04Nb0.86Ta0.10Sb0.04O3-xSrTiO3压电陶瓷进行了钛酸锶掺杂改性研究.使用XRD并结合常规压电陶瓷性能测试手段对该体系的显微结构、压电、介电性能等进行表征.研究结果表明,随着SrTiO3加入量的增大,材料的居里温度和压电性能逐渐下降,材料的介电温度峰形逐渐变宽,出现弛豫现象;陶瓷烧结性能改善.致密度增加.

参考文献

[1] Jaffe B;Marzuilo S;Roth R S .[J].Journal of Applied Physics,1954,25(06):809.
[2] 左铁镛,聂祚仁,狄向华,李贵奇.中国材料环境协调性评价研究进展[J].材料导报,2001(06):1-3.
[3] Bobnar V;Bernard J;Kosec M .[J].Applied Physics Letters,2004,85(06):994.
[4] Zhang S J;Xia R;Shrout T R et al.[J].Journal of Applied Physics,2006,100:104108.
[5] Park H Y;Aim C W;Song H C et al.[J].J Appl Phy,2006,89:062906.
[6] 初宝进,李国荣,江向平,陈大任.Na1/2Bi1/2TiO3-BaTiO3系陶瓷压电性?及弛豫相变研究[J].无机材料学报,2000(05):815-821.
[7] Chu B J;Chen D R;Li G R et al.[J].Journal of the European Ceramic Society,2002,22:2115.
[8] 吴浪,肖定全,赁敦敏,朱建国,余萍,鄢洪建,廖运文,王孝平.[Bi0.5(Na1-xAgx)0.5]1-yBayTiO3系压电陶瓷研究[J].压电与声光,2006(04):455-457.
[9] Kakimoto K I;Izumi M;Hitoshi O .[J].Journal of the European Ceramic Society,2005,25:2719.
[10] Ringgaard E;Wurlitzer T .[J].Journal of the European Ceramic Society,2005,25:2701.
[11] Ivliev M P;Iraevski I P;Reznichenko L A et al.[J].Physics of the Solid State,2003,45(10):1984.
[12] Egerton L;Dillon D M .[J].Journal of the American Ceramic Society,1959,42:438.
[13] Jeager R E;Egerton L .[J].Journal of the American Ceramic Society,1962,45:209.
[14] Yasuyoshl S;Hlsaall T;Toshlhlko T et al.[J].NATURE,2004,432:84.
[15] Matsubara M;Yamaguchi K K.[J].Journal of Applied Physics,2005:97114105.
[16] Hollenstein E;Davis M;Damjanovic D et al.[J].Applied Physics Letters,2005,87:182905.
[17] Guo Y P;Kakimoto K I;Ohsato H .[J].Materials Letters,2005,59:241.
[18] Ichiki M;Zhang L;Tanaka M et al.[J].Journal of the European Ceramic Society,2004,24:1693.
[19] 周晓华,Sфrensen O.Toft,曹全喜,徐毓龙.掺镁钛酸锶 (SrTiO3)陶瓷的导电机理研究[J].无机材料学报,1999(06):927-932.
[20] Hofer C;Weber U;Waser R .[J].Journal of the European Ceramic Society,2001,21:1753.
[21] Guo Y P;Kakimoto K I et al.[J].Solid State Communications,2004,129:279.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%