采用液相浸渍一炭化法制备了沥青基炭/炭复合材料(P-C/C)和沥青一酚醛树脂双基体炭/炭复合材料(D-C/C),研究了它们的增密效率、抗弯强度和摩擦磨损性能的差别。结果表明:P-C/C的增密效率高于D-C/C的;在体积密度基本相同的情况下,两种复合材料的抗弯强度相近;D-C/C的摩擦因数较大,磨损较严重;基体炭结构和性能的差别是造成两种复合材料摩擦磨损性能不同的主要原因。
Pitch-matrix carbon/carbon composites(P-C/C) and pitch & phenolic resin matrix carbon/carbon composites (D-C/C) were prepared using liquid impregnation/carbonization method. Densification efficiency, flexural strength and friction and wear properties of two kinds of carbon/carbon composites were studied. The results show that P-C/C exhibited higher densifieation efficiency than D-C/C. When the volume densities of the two kinds of carbon/carbon composites were the same, no apparent difference was shown in flexural strength. D-C/C showed a higher friction coefficient and fairly serious wear. The difference of structures and properties of matrix carbon caused different friction and wear properties of these two kinds of carbon/carbon composites mainly.
参考文献
[1] | 李贺军,曾燮榕,李克智,张秀莲.我国炭/炭复合材料研究进展[J].炭素,2001(04):8-13. |
[2] | J. NEUMEISTER;S. JANSSON;F. LECKIE .THE EFFECT OF FIBER ARCHITECTURE ON THE MECHANICAL PROPERTIES OF CARBON/CARBON FIBER COMPOSITES[J].Acta materialia,1996(2):573-585. |
[3] | 易茂中,葛毅成,冯一雷,黄启忠,黄伯云.C/C复合材料及高强石墨高温摩擦磨损性能对比研究[J].摩擦学学报,2004(03):235-239. |
[4] | 葛毅成,易茂中,黄伯云,李丽娅.润滑状态对C/C复合材料摩擦磨损特性的影响[J].中国有色金属学报,2004(08):1405-1409. |
[5] | 周绍建,苏君明,苏哲安,李瑞珍,崔红.树脂炭含量对C/C复合材料性能的影响[J].新型炭材料,2001(01):49-52. |
[6] | 陈腾飞,龚伟平,刘根山,黄玉东,王超.基体炭结构对炭/炭复合材料的界面结合强度的影响[J].矿冶工程,2004(01):77-79. |
[7] | 于澍,张红波,熊翔,黄伯云,张传福,曾维亚.炭/炭刹车副表面硬度对摩擦磨损性能的影响[J].功能材料,2006(09):1459-1462. |
[8] | 胡志彪,李贺军,陈强,李克智,黄荔海.碳/碳复合材料摩擦学性能及摩擦机制研究进展[J].材料工程,2004(12):59-62. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%