为了研究轧制工艺对WNQ570桥梁钢再结晶行为的影响,采用Gleeble-3500热模拟试验机模拟了其双道次热变形过程,测试了试验钢的应力-应变曲线,建立了静态再结晶晶粒体积分数随变形温度和道次间隔时间变化的关系模型,分析了应变诱导析出抑制对静态软化行为的影响。研究结果表明：静态再结晶体积分数随变形温度的提高或道次间隔时间的延长而增大,应变诱导析出抑制静态再结晶的进行;静态再结晶激活能为240.47kJ/mol。研究结果为制订试验钢二阶段控轧工艺提供了依据。
In order to study the effect of rolling process on the recrystallization behavior of WNQ570 steel for bridge,the two-pass hot deformation of WNQ570 steel for bridge was carried out using Gleeble-3500 thermal/mechanical simulator,and the stress-strain curves for the steel were obtained.One model for estimating the volume fraction of static recrystal grains varied with deformation temperature and interval time was developed.Meanwhile,the effect of stain induced precipitation on softening behavior of static recrystallization was analyzed.The results show that the volume fraction of recrystal grains increases with the deformation temperature or the interval time.The static recrystallization behavior is inhibited from the precipitation of fine particles.The activation energy for static recrystallization is determined as 240.47 kJ/ mol.The results can be used as the reference for design of the two-stage rolling scheme.
参考文献
| [1] | 郭爱民.我国铁路桥梁用钢的发展现状及展望[J].铁路采购与物流,2007(12):25-26. |
| [2] | 尚成嘉,杨善武,王学敏,贺信莱.新颖的贝氏体/铁素体双相低碳微合金钢[J].北京科技大学学报,2003(03):288-290. |
| [3] | 蔺永诚,陈明松,钟掘.42CrMo钢亚动态再结晶行为研究[J].材料热处理学报,2009(02):71-75. |
| [4] | Jones J J.Effect of Interpass Time on the Hot Roiling Behav- ior of Mieroalloyed Steels[A].Switzeland.Trans Tech Publication,1998:284-286. |
| [5] | W.P.SUN .Comparison between Static and Metadynamic Recrystallization-An Application to the Hot Rolling of Steels[J].ISIJ International,1997(10):1000-1009. |
| [6] | 刘文斌,康永林,牛涛,李彬.热连轧生产厚规格X80管线钢的静态再结晶行为及工艺优化[J].北京科技大学学报,2010(04):444-449. |
| [7] | 王瑞珍,杨忠民,车彦民.低碳钢Q235形变奥氏体的静态再结晶[J].钢铁研究学报,2006(03):33-37. |
| [8] | 宁小智,王立民,刘正东,杨钢,张家涛.403Nb叶片钢高温热压缩静态再结晶研究[J].钢铁,2009(02):69-71. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%