分别采用原子层沉积(ALD)和磁控溅射法(MS)在Si和石英衬底上制备TiO2薄膜,并进行退火处理.利用X射线衍射仪(XRD)、扫描电子显微镜(SEM)、原子力显微镜(AFM)和紫外分光光度计对这两种方法制备薄膜的晶型结构、表面形貌和光学特性进行分析对比.结果显示,对于沉积态TiO2薄膜,ALD-TiO2和MS-TiO2未能检测到TiO2衍射峰.ALD-TiO2为颗粒膜,其表面粗糙,颗粒尺寸大;MS-TiO2薄膜表面平整.经退火后,两种方法制备的TiO2薄膜能检测到锐钛矿A(101)衍射峰,但结晶质量不高.受薄膜表面形貌和晶型结构等因素影响,退火前后ALD-TiO2透过率与MS-TiO2透过率变化不一致.对于沉积态和退火态薄膜的禁带宽度,ALD-TiO2分别为3.8eV和3.7 eV,吸收边带发生红移,MS-TiO2分别为3.74 eV和3.84 eV,吸收边带发生蓝移.
参考文献
| [1] | Andrew Mills;Soo-Keun Lee.A web-based overview of semiconductor photochemistry-based current commercial applications[J].Journal of Photochemistry and Photobiology, A. Chemistry,20021/3(1/3):233-247. |
| [2] | Michael R. Hoffmann;Scot T. Martin;Wonyong Choi;Detlef W. Bahnemann.Environmental Applications of Semiconductor Photocatalysis[J].Chemical Reviews,19951(1):69-96. |
| [3] | 彭寿;操芳芳;金良茂.Fe3+/TiO2纳米薄膜的亲水性及光催化性能[J].纳米技术与精密工程,2014(6):449-454. |
| [4] | 张一兵;郑敏;蒋荣彬;江雷.掺Fe3+A-TiO2粉末的水热法制备及其光催化降解甲基橙[J].生态环境学报,2010(7):1700-1703. |
| [5] | 张万忠;刘景民;周智敏.纳米TiO2的研究与应用进展[J].石油化工,2007(11):1184-1190. |
| [6] | 李建国;惠龙飞;冯昊;秦利军;龚婷;安忠维.原子层沉积制备VO2薄膜及特性研究[J].真空科学与技术学报,2015(2):243-249. |
| [7] | 魏呵呵;何刚;邓彬;李文东;李太申.原子层沉积技术的发展现状及应用前景[J].真空科学与技术学报,2014(4):413-420. |
| [8] | Shahab Ansari Amin;Mohammad Pazouki;Azarmidokht Hosseinnia.Synthesis of TiO2-Ag nanocomposite with sol-gel method and investigation of its antibacterial activity against E. coli[J].Powder Technology: An International Journal on the Science and Technology of Wet and Dry Particulate Systems,20093(3):241-245. |
| [9] | 贺蕴秋;王德平;林健.溶胶-凝胶TiO2的晶相转变温度[J].功能材料,2000(2):149-152. |
| [10] | Sammelselg V.;Tarre A.;Niinisto L.;Heiskanen K.;Ilmonen K.;Johansson LS.;Uustare T.;Rosental A..TiO2 thin films by atomic layer deposition: a case of uneven growth at low temperature[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,19981/4(1/4):78-86. |
| [11] | 朱明海;陈广彬;冯禹;龚楠;汪剑波.磁控溅射制备Ti-Zn-O复合薄膜及其光学性质研究[J].长春理工大学学报（自然科学版）,2014(1):48-51. |
| [12] | Hwa-Jong Lee;Jung-A Lee;Joon-Hyung Lee.Optical band gap modulation by Mg-doping in In_2O_3(ZnO)_3 ceramics[J].CERAMICS INTERNATIONAL,20128(8):6693-6697. |
| [13] | 段文芳;赵小如;段利兵;白晓军;史小龙;朱宇瑾;孙慧楠.退火气氛和镧掺杂浓度对ZnO薄膜结构和光学性能的影响[J].人工晶体学报,2013(8):1515-1520,1525. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%