介绍了典型的极不相容共混物(EIB)聚乙烯/聚碳酸酯(PE/PC)体系的形态受组成的影响,以及共混物在受到拉伸前后、冲击前后的形态.通过扫描电子显微镜(SEM)观察发现,组成不仅影响分散相粒子的大小、形状,还决定分散相与连续相的转变;共混物在受到拉应力(拉伸)和剪切应力(冲击)后,前者较多球状粒子变形成为有利于提高拉伸性能的纤维状,后者粒子和基体都发生了能提高抗冲击韧性的塑性变形.
参考文献
| [1] | Cheung P;Suwanda D;Balke S T .[J].Polymer Engineering and Science,1990,30(17):1063-1071. |
| [2] | 江明.高分子合金的物理化学[M].成都:四川教育出版社,1988:1-8. |
| [3] | Min K;White J L;Fellers J F .[J].Journal of Applied Polymer Science,1984,29:2117-2125. |
| [4] | Endo S;Min K;White J L .[J].Polymer Engineering and Science,1986,26:45-53. |
| [5] | Min K;White J L;Fellers J F .[J].Polymer Engineering and Science,1984,24:1327-1334. |
| [6] | Favis B D;Therien D .[J].POLYMER,1991,32:1474-1481. |
| [7] | Fisa B;Favis B D;Bourgeois S .[J].Polymer Engineering and Science,1990,30:1051-1062. |
| [8] | Mekhilef N;Ait-Kadi A;Ajji A .[J].Polymer Engineering and Science,1992,32:894-898. |
| [9] | Willis J M;Favis B D .[J].Polymer Engineering and Science,1988,28:1416-1456. |
| [10] | Favis B D;Lavallee C J .[J].Journal of Materials Science,1992,27:1211-1228. |
| [11] | Favis B D;Chalifoux J D .[J].Polymer,1988,29:1761-1779. |
| [12] | 李忠明,杨呜波,冯建民.烯基双酚A醚接枝LDPE的研究[J].高分子材料科学与工程,1997(06):114-119. |
| [13] | Yang Mingbo;Li Zhongming;Feng Jianming .[J].Polymer Engineering and Science,1998,38(06):879-885. |
| [14] | 杨鸣波,李忠明,冯建民,李光宪.含二烯丙基双酚A醚相容剂对HDPE/PC共混体系的影响[J].高分子学报,1999(01):113-117. |
| [15] | 杨鸣波;李忠明;冯建民 .[J].中国塑料,1996,10(03):38-44. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%